Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 12, Part 3American Society of Mechanical Engineers, 1993 - Arctic regions |
From inside the book
Results 1-3 of 74
Page 1
... yield strength steel plate for offshore struc- tures . The degree of yield strength matching influences the overall performance of welded joints only in ductile mode . The CTOD values obtained by the three point bend and the through ...
... yield strength steel plate for offshore struc- tures . The degree of yield strength matching influences the overall performance of welded joints only in ductile mode . The CTOD values obtained by the three point bend and the through ...
Page 76
... yield strength require- ment . The higher preheat and interpass temperature , and thus slower cooling rates , also provide a more severe test of the yield strength of this system . All - weld- metal tensile properties and Charpy V ...
... yield strength require- ment . The higher preheat and interpass temperature , and thus slower cooling rates , also provide a more severe test of the yield strength of this system . All - weld- metal tensile properties and Charpy V ...
Page 621
... yield strength of weld metal H , indicating that its alloy system is not sensitive to cooling rate . For both plate and weld metal it was found that increasing yield strengths are associated with a sub- stantial increase in yield to ...
... yield strength of weld metal H , indicating that its alloy system is not sensitive to cooling rate . For both plate and weld metal it was found that increasing yield strengths are associated with a sub- stantial increase in yield to ...
Contents
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 7 |
HIGH STRENGTH STEELS FOR OFFSHORE | 189 |
Weldability of NitrogenEnhanced HSLA Steels | 231 |
Copyright | |
18 other sections not shown
Other editions - View all
Common terms and phrases
alloy analysis applied argon artificial neural network ASTM austenite austenite grain bainite base metal behaviour bending CGHAZ Charpy composite pipe cooling corrosion crack propagation CTOD curve cycles developed diameter effect elastomer electrodes Engineering ASME 1993 epoxy equation experimental fabrication factor ferrite firewater firewater system flange fracture fracture mechanics GRE pipe heat input high strength steels HSLA HSLA steels hydrogen increase initial installation intumescent kJ/mm load martensite Materials Engineering ASME maximum method microstructure MIRT nitrogen nitrogen steel node notch offshore structures OMAE parameters performance predicted preheat pressure procedures PWHT range reduced S-N curves seal seawater sheave shielding gas shown in Figure simulated SINTEF specimens spool stainless steel strain surface Table Technology temperature tensile test results thickness toughness tubular joints underwater Underwater Welding values weld metal weldability welded joints weldments wet welding wide plate wire yield strength