... critical CTOD for the weld HAZ of the materials was obtained using the standard Bx2B CTOD specimens according to BS5762 . The specimens had a through - thickness machined notch , which has the same notch - tip geometry as for the wide ...
... critical CTOD for the weld HAZ of the materials was obtained using the standard Bx2B CTOD specimens according to BS5762 . The specimens had a through - thickness machined notch , which has the same notch - tip geometry as for the wide ...
Page 258
... critical CTOD values of weld HAZ quantitatively among the various steel plates . In the present study , the critical CTOD for weld HAZ of various steels with a sufficient data for the statistical analysis was used . Fracture toughness ...
... critical CTOD values of weld HAZ quantitatively among the various steel plates . In the present study , the critical CTOD for weld HAZ of various steels with a sufficient data for the statistical analysis was used . Fracture toughness ...
Page 269
... critical tooth of a pre - loaded connection varies as axial load is applied from zero to its maximum value . However ... critical tooth Critical tooth number Kti Stress concentration factor at tooth i , i.e. Kti = σi / Si = Ktc Stress ...
... critical tooth of a pre - loaded connection varies as axial load is applied from zero to its maximum value . However ... critical tooth Critical tooth number Kti Stress concentration factor at tooth i , i.e. Kti = σi / Si = Ktc Stress ...
Contents
ADVANCED COMPOSITES | 1 |
Probabilistic Aspects of HAZ CTOD Value of Multipass Welded Joint of Steel for Offshore | 5 |
The Use of GRP Materials in Platform Topsides Construction and the Regulatory Implications | 15 |
35 other sections not shown
Other editions - View all
Common terms and phrases
analysis applications as-welded ASTM axial load behaviour bending brace calculated chord Composite Materials compressive strength corrosion rate crack growth CTOD cycles damage delamination elastomer Engineering environment epoxy experimental failure fatigue crack fatigue design fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness geometry increase initial installation interlaminar fracture laminate layers marine matrix maximum mean stress method Mode modulus moisture nodes nominal notch obtained offshore structures optical fiber parameters performance phenolic pipe plate thickness platform pre-load predicted pressure principal stress pultrusion rebar reinforcement resin resistance riser rubber S-N curves sea water seal shear stress shell shown in Fig space frame specimens steel strain stress concentration stress concentration factor stress range surface crack Table techniques tensile strength tension thickness effect thread tube tubular joints values water mixed concrete weight weld toe welded joints yield strength zone