... Fatigue . Fatigue failure is hardly ever observed on any real life concrete structure . of Fatigue resistance concrete structures exposed to dynamic cracking seems well covered by recognized verification procedures . S - N curves ...
... Fatigue . Fatigue failure is hardly ever observed on any real life concrete structure . of Fatigue resistance concrete structures exposed to dynamic cracking seems well covered by recognized verification procedures . S - N curves ...
Page 202
3 . specimens , fatigue life cathodically protected was the same as freely corroding , irrespective of whether the profile was controlled or uncontrolled . Comparison of the present fatigue data with the AWS Code suggests that the ...
3 . specimens , fatigue life cathodically protected was the same as freely corroding , irrespective of whether the profile was controlled or uncontrolled . Comparison of the present fatigue data with the AWS Code suggests that the ...
Page 222
... Fatigue Strength with Regard to the Statistical Size Effect " , ( in German ) , Zeitschrift f . Werkstofftech- nik , No.13 , 1982 , p.120-128 . 11. Kloos , K.H. , Buch , A. and Zankov , D .: " Pure geometric size effect in fatigue tests ...
... Fatigue Strength with Regard to the Statistical Size Effect " , ( in German ) , Zeitschrift f . Werkstofftech- nik , No.13 , 1982 , p.120-128 . 11. Kloos , K.H. , Buch , A. and Zankov , D .: " Pure geometric size effect in fatigue tests ...
Contents
ADVANCED COMPOSITES | 1 |
Probabilistic Aspects of HAZ CTOD Value of Multipass Welded Joint of Steel for Offshore | 5 |
The Use of GRP Materials in Platform Topsides Construction and the Regulatory Implications | 15 |
35 other sections not shown
Other editions - View all
Common terms and phrases
analysis applications as-welded ASTM axial load behaviour bending brace calculated chord Composite Materials compressive strength corrosion rate crack growth CTOD cycles damage delamination elastomer Engineering environment epoxy experimental failure fatigue crack fatigue design fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness geometry increase initial installation interlaminar fracture laminate layers marine matrix maximum mean stress method Mode modulus moisture nodes nominal notch obtained offshore structures optical fiber parameters performance phenolic pipe plate thickness platform pre-load predicted pressure principal stress pultrusion rebar reinforcement resin resistance riser rubber S-N curves sea water seal shear stress shell shown in Fig space frame specimens steel strain stress concentration stress concentration factor stress range surface crack Table techniques tensile strength tension thickness effect thread tube tubular joints values water mixed concrete weight weld toe welded joints yield strength zone