... fibers . A different technique uses a few- mode fiber to eliminate the reference leg of the interferometer , at some cost in ultimate sensitivity ( 6-8 ) . The few - mode fibers are typically quite similar physically to single - mode fibers ...
... fibers . A different technique uses a few- mode fiber to eliminate the reference leg of the interferometer , at some cost in ultimate sensitivity ( 6-8 ) . The few - mode fibers are typically quite similar physically to single - mode fibers ...
Page 53
... fiber : A ) Uniaxial carbon fiber / vinyl ester matrix composite rod 5 mm in diameter ; B ) Epoxy potting resin ; C ) Region of initial failure at the interface between A ) and B ) ; D ) Embedded multimode optical fiber . FRACTOGRAPHY A ...
... fiber : A ) Uniaxial carbon fiber / vinyl ester matrix composite rod 5 mm in diameter ; B ) Epoxy potting resin ; C ) Region of initial failure at the interface between A ) and B ) ; D ) Embedded multimode optical fiber . FRACTOGRAPHY A ...
Page 54
graphite fiber used in the present investigation was much less than the ultimate strain of the optical fiber . It is anticipated that a closer match of strain capability would yield a more sensitive detector of incipient failure . Work ...
graphite fiber used in the present investigation was much less than the ultimate strain of the optical fiber . It is anticipated that a closer match of strain capability would yield a more sensitive detector of incipient failure . Work ...
Contents
ADVANCED COMPOSITES | 1 |
Probabilistic Aspects of HAZ CTOD Value of Multipass Welded Joint of Steel for Offshore | 5 |
The Use of GRP Materials in Platform Topsides Construction and the Regulatory Implications | 15 |
35 other sections not shown
Other editions - View all
Common terms and phrases
analysis applications axial behaviour bending brace calculated carried chord combined compared components composite Composite Materials compression concrete connection considered construction corrosion crack crack growth critical curve cycles damage determined developed distribution effect element Engineering experimental factor failure fatigue fiber Figure finite element force fracture geometry increase indicate initial internal laminate length limit load lower Marine material matrix maximum mean measured mechanical method Mode nodes nominal normal observed obtained offshore operation parameters performance pipe plate platform position predicted present pressure production properties range ratio reduced reinforcement Research resin resistance seal shear shell shown shows specimen steel stiffener stiffness strain strength stress concentration structures surface Table techniques temperature tensile tension thickness thread tube tubular joints weight weld