Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 9American Society of Mechanical Engineers, 1990 - Arctic regions |
From inside the book
Results 1-3 of 64
Page 234
... predicted identical fatigue lives for all three loading paths . The nominal von Mises approach predicted identical fatigue lives for loading paths F and J , while predicting an increased fatigue damage for loading path I. Only the ...
... predicted identical fatigue lives for all three loading paths . The nominal von Mises approach predicted identical fatigue lives for loading paths F and J , while predicting an increased fatigue damage for loading path I. Only the ...
Page 236
... predicted for both loading cases . The macroscopic crack growth reflects the At orientation predicted by the Findley model . At the onset of final failure , cracking occurred again on the maximum shear stress orientation . CONCLUSIONS ...
... predicted for both loading cases . The macroscopic crack growth reflects the At orientation predicted by the Findley model . At the onset of final failure , cracking occurred again on the maximum shear stress orientation . CONCLUSIONS ...
Page 383
... Predicted and Tested Crack Growth ( Specimen No. W6-20 ) Fig . 8 Comparison of Predicted and Tested Fatigue Lives of Tubular T - Joints 10 20 PREDICTION TWI TEST NORMALIZED CRACK DEPTH , a / T 1.0 106 PREDICTED FATIGUE CYCLES 107 30 0.8 ...
... Predicted and Tested Crack Growth ( Specimen No. W6-20 ) Fig . 8 Comparison of Predicted and Tested Fatigue Lives of Tubular T - Joints 10 20 PREDICTION TWI TEST NORMALIZED CRACK DEPTH , a / T 1.0 106 PREDICTED FATIGUE CYCLES 107 30 0.8 ...
Contents
ADVANCED COMPOSITES | 1 |
Probabilistic Aspects of HAZ CTOD Value of Multipass Welded Joint of Steel for Offshore | 5 |
The Use of GRP Materials in Platform Topsides Construction and the Regulatory Implications | 15 |
35 other sections not shown
Other editions - View all
Common terms and phrases
analysis applications as-welded ASTM axial load behaviour bending brace calculated chord Composite Materials compressive strength corrosion rate crack growth CTOD cycles damage delamination elastomer Engineering environment epoxy experimental failure fatigue crack fatigue design fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness geometry increase initial installation interlaminar fracture laminate layers marine matrix maximum mean stress method Mode modulus moisture nodes nominal notch obtained offshore structures optical fiber parameters performance phenolic pipe plate thickness platform pre-load predicted pressure principal stress pultrusion rebar reinforcement resin resistance riser rubber S-N curves sea water seal shear stress shell shown in Fig space frame specimens steel strain stress concentration stress concentration factor stress range surface crack Table techniques tensile strength tension thickness effect thread tube tubular joints values water mixed concrete weight weld toe welded joints yield strength zone