... resins readily burn . When fire safety is a concern , the traditional approach has been to add fire - retardant fillers to the resin . These additives can decrease the flammability of the resin ; however , they often increase the ...
... resins readily burn . When fire safety is a concern , the traditional approach has been to add fire - retardant fillers to the resin . These additives can decrease the flammability of the resin ; however , they often increase the ...
Page 24
... resin which would wet the laminate . ACT has eliminated this portion of the process , and instead passes the dry fibers through a pre - heater which raises the reinforcing material's temperature to facilitate better wetting by the resin ...
... resin which would wet the laminate . ACT has eliminated this portion of the process , and instead passes the dry fibers through a pre - heater which raises the reinforcing material's temperature to facilitate better wetting by the resin ...
Page 25
... resin in the bath to cure . It is therefore not practical to impregnate the fiber materials at elevated temperature using wet - bath technology . Wet bath impregnation of reinforcing fibers has other drawbacks as well . Many resin ...
... resin in the bath to cure . It is therefore not practical to impregnate the fiber materials at elevated temperature using wet - bath technology . Wet bath impregnation of reinforcing fibers has other drawbacks as well . Many resin ...
Contents
ADVANCED COMPOSITES | 1 |
Probabilistic Aspects of HAZ CTOD Value of Multipass Welded Joint of Steel for Offshore | 5 |
The Use of GRP Materials in Platform Topsides Construction and the Regulatory Implications | 15 |
35 other sections not shown
Other editions - View all
Common terms and phrases
analysis applications as-welded ASTM axial load behaviour bending brace calculated chord Composite Materials compressive strength corrosion rate crack growth CTOD cycles damage delamination elastomer Engineering environment epoxy experimental failure fatigue crack fatigue design fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness geometry increase initial installation interlaminar fracture laminate layers marine matrix maximum mean stress method Mode modulus moisture nodes nominal notch obtained offshore structures optical fiber parameters performance phenolic pipe plate thickness platform pre-load predicted pressure principal stress pultrusion rebar reinforcement resin resistance riser rubber S-N curves sea water seal shear stress shell shown in Fig space frame specimens steel strain stress concentration stress concentration factor stress range surface crack Table techniques tensile strength tension thickness effect thread tube tubular joints values water mixed concrete weight weld toe welded joints yield strength zone