... seal performance . In fact , low temperature seal performance did not correlate with brittle point or either of the Gehman transition temperatures . In this test , seals of four compounds failed well above corresponding brittle point ...
... seal performance . In fact , low temperature seal performance did not correlate with brittle point or either of the Gehman transition temperatures . In this test , seals of four compounds failed well above corresponding brittle point ...
Page 162
... seal is installed on casing at low tolerance conditions . Also , the seal gland in the wellhead equipment is a fixed dimension requiring the seal to be easily installed and function over a range of squeeze values , typically from 7 % to ...
... seal is installed on casing at low tolerance conditions . Also , the seal gland in the wellhead equipment is a fixed dimension requiring the seal to be easily installed and function over a range of squeeze values , typically from 7 % to ...
Page 163
... seal can compensate for thermal expansion , allow easy installation and will also provide automatic energization by expanding the seal elements radially as externally applied pressure is increased . This feature is most useful in ...
... seal can compensate for thermal expansion , allow easy installation and will also provide automatic energization by expanding the seal elements radially as externally applied pressure is increased . This feature is most useful in ...
Contents
ADVANCED COMPOSITES | 1 |
Probabilistic Aspects of HAZ CTOD Value of Multipass Welded Joint of Steel for Offshore | 5 |
The Use of GRP Materials in Platform Topsides Construction and the Regulatory Implications | 15 |
35 other sections not shown
Other editions - View all
Common terms and phrases
analysis applications as-welded ASTM axial load behaviour bending brace calculated chord Composite Materials compressive strength corrosion rate crack growth CTOD cycles damage delamination elastomer Engineering environment epoxy experimental failure fatigue crack fatigue design fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness geometry increase initial installation interlaminar fracture laminate layers marine matrix maximum mean stress method Mode modulus moisture nodes nominal notch obtained offshore structures optical fiber parameters performance phenolic pipe plate thickness platform pre-load predicted pressure principal stress pultrusion rebar reinforcement resin resistance riser rubber S-N curves sea water seal shear stress shell shown in Fig space frame specimens steel strain stress concentration stress concentration factor stress range surface crack Table techniques tensile strength tension thickness effect thread tube tubular joints values water mixed concrete weight weld toe welded joints yield strength zone