Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 9American Society of Mechanical Engineers, 1990 - Arctic regions |
From inside the book
Results 1-3 of 47
Page 229
... shear stress amplitude , maximum principal stress amplitude ( deg . ) Bending stress to torsional stress ratio Nominal bending , torsional stress range ( MPa ) Nominal bending , shear stress amplitude ( MPa ) Ασ Aomax 40 off 1 2 2 Δσ 1 ...
... shear stress amplitude , maximum principal stress amplitude ( deg . ) Bending stress to torsional stress ratio Nominal bending , torsional stress range ( MPa ) Nominal bending , shear stress amplitude ( MPa ) Ασ Aomax 40 off 1 2 2 Δσ 1 ...
Page 232
... shear stress orientations , respectively . The orientation of the maximum principal stress amplitude is at an angle from the longitudinal specimen axis where there is no shear . There are normal and shear stresses on all other ...
... shear stress orientations , respectively . The orientation of the maximum principal stress amplitude is at an angle from the longitudinal specimen axis where there is no shear . There are normal and shear stresses on all other ...
Page 234
... shear stress range . Even though the fatigue cracking was confined to the weld toe for all in - phase tests , the final fracture surface had a " factory roof " appearance . The fatigue cracks initiated in the plane of the weld toe or ...
... shear stress range . Even though the fatigue cracking was confined to the weld toe for all in - phase tests , the final fracture surface had a " factory roof " appearance . The fatigue cracks initiated in the plane of the weld toe or ...
Contents
ADVANCED COMPOSITES | 1 |
Probabilistic Aspects of HAZ CTOD Value of Multipass Welded Joint of Steel for Offshore | 5 |
The Use of GRP Materials in Platform Topsides Construction and the Regulatory Implications | 15 |
35 other sections not shown
Other editions - View all
Common terms and phrases
analysis applications as-welded ASTM axial load behaviour bending brace calculated chord Composite Materials compressive strength corrosion rate crack growth CTOD cycles damage delamination elastomer Engineering environment epoxy experimental failure fatigue crack fatigue design fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness geometry increase initial installation interlaminar fracture laminate layers marine matrix maximum mean stress method Mode modulus moisture nodes nominal notch obtained offshore structures optical fiber parameters performance phenolic pipe plate thickness platform pre-load predicted pressure principal stress pultrusion rebar reinforcement resin resistance riser rubber S-N curves sea water seal shear stress shell shown in Fig space frame specimens steel strain stress concentration stress concentration factor stress range surface crack Table techniques tensile strength tension thickness effect thread tube tubular joints values water mixed concrete weight weld toe welded joints yield strength zone