... Charpy and CTOD values by plotting minimum single mid - thickness CGZ Charpy results against minimum single CTOD values , but no correlation was established . In practice , correlation between Charpy and CTOD data is only possible if ...
... Charpy and CTOD values by plotting minimum single mid - thickness CGZ Charpy results against minimum single CTOD values , but no correlation was established . In practice , correlation between Charpy and CTOD data is only possible if ...
Page 124
... Charpy values of less than 100J at -40 ° C . Examining the HAZ Charpy results for these plates shows that they had generally poorer toughness in the welded condition than the normal toughness plates . Relationship Toughness Between ...
... Charpy values of less than 100J at -40 ° C . Examining the HAZ Charpy results for these plates shows that they had generally poorer toughness in the welded condition than the normal toughness plates . Relationship Toughness Between ...
Page 188
... Charpy - v- toughness at + 40 ° c < 27 27-50 50-100 100-150 150-200 > 200 Figure 4 : Statistical presentation of the Charpy - V - fracture toughness test results . NUMBER OF SPECIMENS 32 Spec . 45 24 16 8 0 45 145 245 345 445 ( J ) CHARPY ...
... Charpy - v- toughness at + 40 ° c < 27 27-50 50-100 100-150 150-200 > 200 Figure 4 : Statistical presentation of the Charpy - V - fracture toughness test results . NUMBER OF SPECIMENS 32 Spec . 45 24 16 8 0 45 145 245 345 445 ( J ) CHARPY ...
Contents
ADVANCED COMPOSITES | 1 |
A Study of the MultiLayered GRP Composite Cylindrical Vessel | 13 |
Resistance of Composite Structures to Impact Loads | 19 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
abrasion analysis as-welded assessment austenite axial base metal behaviour bending boron brittle fracture brittle zones CGHAZ Charpy chemical composition chord coarse grained HAZ concrete Conference on Offshore crack growth crack length CTOD tests CTOD values curve cycle defect effect fabrication ferrite fiber Figure fracture initiation fracture mechanics fracture toughness fusion line grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen ICCGHAZ impact increase layup load low carbon low toughness martensite material maximum Mechanics and Arctic method niobium Offshore Mechanics offshore structures Oseberg parameters plastic plate thickness pop-in post weld heat preheat PWHT region residual stresses sampled simulated solidification cracking steel plates stiffeners stress concentration stress intensity factor submerged arc welding surface notched Table temperature tensile thermal TMCP transverse tubular joints weld metal weld toe weldability welded joints welding procedures weldments wide plate tests yield strength