... Charpy and CTOD values by plotting minimum single mid - thickness CGZ Charpy results against minimum single CTOD values , but no correlation was established . In practice , correlation between Charpy and CTOD data is only possible if ...
... Charpy and CTOD values by plotting minimum single mid - thickness CGZ Charpy results against minimum single CTOD values , but no correlation was established . In practice , correlation between Charpy and CTOD data is only possible if ...
Page 124
... Charpy values of less than 100J at -40 ° C . Examining the HAZ Charpy results for these plates shows that they had generally poorer toughness in the welded condition than the normal toughness plates . Relationship Toughness Between ...
... Charpy values of less than 100J at -40 ° C . Examining the HAZ Charpy results for these plates shows that they had generally poorer toughness in the welded condition than the normal toughness plates . Relationship Toughness Between ...
Page 188
... Charpy- v - toughness at + 40 ° c b ) FL + 2 < 27 27-50 50-100 100-150 150-200 > 200 Charpy- v - toughness at + 40 ° c 150 Number of specimens 100 50 100 Number of 80 specimens 60 40 20 < 0.1 0.1-0.2 0.2-0.4 0.4-0.7 0.7-1.0 > 1.0 a ...
... Charpy- v - toughness at + 40 ° c b ) FL + 2 < 27 27-50 50-100 100-150 150-200 > 200 Charpy- v - toughness at + 40 ° c 150 Number of specimens 100 50 100 Number of 80 specimens 60 40 20 < 0.1 0.1-0.2 0.2-0.4 0.4-0.7 0.7-1.0 > 1.0 a ...
Contents
ADVANCED COMPOSITES | 1 |
PAS2m High Performance Prepreg and Composites | 9 |
ADVANCES IN WELDING TECHNOLOGY | 31 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
abrasion analysis Arctic Engineering as-welded assessment austenite axial behaviour bending brittle fracture brittle zones CGHAZ Charpy chord coarse grained HAZ concrete Conference on Offshore corrosion fatigue crack depth crack length crack propagation CTOD tests CTOD values curve cycles defect effect fabrication ferrite fiber Figure fracture initiation fracture mechanics fracture toughness fusion line geometry grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen ICCGHAZ impact increase load low carbon low toughness martensite material maximum Mechanics and Arctic niobium Offshore Mechanics offshore structures Oseberg parameters plastic plate thickness pop-in post weld heat preheat PWHT region residual stresses S-N curves sampled simulated steel plates stiffeners stress concentration stress intensity factor structural steels submerged arc welding surface notched Table temperature tensile thermal TMCP tubular joints weld metal weld toe weldability welded joints welding procedures weldments wide plate tests yield strength