... brittle fracture , fig 13 . The majority of brittle fractures were preferenti- ally initiated in the coarse grained zone close to the fusion line , fig 14. The reference steel revealed also brittle fracture initiating from the partially ...
... brittle fracture , fig 13 . The majority of brittle fractures were preferenti- ally initiated in the coarse grained zone close to the fusion line , fig 14. The reference steel revealed also brittle fracture initiating from the partially ...
Page 379
... brittle zones low toughness these of regions ( LBZs ) are brittle microstructure within the heat affected zones ( HAZS ) of steel weldments that can initiate brittle This levels . fracture paper describes the metallurgical nature of ...
... brittle zones low toughness these of regions ( LBZs ) are brittle microstructure within the heat affected zones ( HAZS ) of steel weldments that can initiate brittle This levels . fracture paper describes the metallurgical nature of ...
Page 522
... brittle zone ( tp ) on CTOD value . While CTOD value changed little with to greater than 2mm or 4mm , depending on ... brittle zone is constant irrespective of t . am , on the other hand , changes with to . Om at the brittle zone is more ...
... brittle zone ( tp ) on CTOD value . While CTOD value changed little with to greater than 2mm or 4mm , depending on ... brittle zone is constant irrespective of t . am , on the other hand , changes with to . Om at the brittle zone is more ...
Contents
ADVANCED COMPOSITES | 1 |
A Study of the MultiLayered GRP Composite Cylindrical Vessel | 13 |
Resistance of Composite Structures to Impact Loads | 19 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
addition analysis applied areas assessment base bending brittle calculated carbon carried Charpy chemical chord coarse grained compared composite concrete considered cooling crack tip critical CTOD curve cycle defect depth determined developed direction distribution effect element energy Engineering examined fabrication factor failure fatigue crack ferrite Figure fracture mechanics fracture toughness fusion geometry growth hardness heat input higher impact increase initiation length load lower material maximum measured Mechanics method microstructures normal notch observed obtained occur offshore parameters performed plastic plate position present pressure problem procedure production properties range reduced region Research respectively sampled shown shows simulated specific specimens steel steel plates stiffeners strain strength stress structures surface Table temperature tensile thickness tubular values weld metal welded joints weldments wide yield zone