... compared to steels A , B and C possesses superior Charpy impact properties in its as - received condition . As would be expected , the transition temperature after simulation shift to higher temperatures ( Figs . 6 and 7 ) . The extent ...
... compared to steels A , B and C possesses superior Charpy impact properties in its as - received condition . As would be expected , the transition temperature after simulation shift to higher temperatures ( Figs . 6 and 7 ) . The extent ...
Page 215
... compared to the plate mate- rial curves , a noticeable difference in their shape . First , the limit of proportionality , i.e. the stress at which the stress - strain curve departs from linearity , as compared to the base material's ...
... compared to the plate mate- rial curves , a noticeable difference in their shape . First , the limit of proportionality , i.e. the stress at which the stress - strain curve departs from linearity , as compared to the base material's ...
Page 278
... compared with the previous results ( 6 ) , fig 7f , and a close inspection of the specimens revealed that the width of the coarse grained zone at the notch tip was narrow , table 3. In order to increase the width of Table 3 . The width ...
... compared with the previous results ( 6 ) , fig 7f , and a close inspection of the specimens revealed that the width of the coarse grained zone at the notch tip was narrow , table 3. In order to increase the width of Table 3 . The width ...
Contents
ADVANCED COMPOSITES | 1 |
A Study of the MultiLayered GRP Composite Cylindrical Vessel | 13 |
Resistance of Composite Structures to Impact Loads | 19 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
addition analysis applied areas assessment base bending brittle calculated carbon carried Charpy chemical chord coarse grained compared composite concrete considered cooling crack tip critical CTOD curve cycle defect depth determined developed direction distribution effect element energy Engineering examined fabrication factor failure fatigue crack ferrite Figure fracture mechanics fracture toughness fusion geometry growth hardness heat input higher impact increase initiation length load lower material maximum measured Mechanics method microstructures normal notch observed obtained occur offshore parameters performed plastic plate position present pressure problem procedure production properties range reduced region Research respectively sampled shown shows simulated specific specimens steel steel plates stiffeners strain strength stress structures surface Table temperature tensile thickness tubular values weld metal welded joints weldments wide yield zone