... developed and applied to fabrication of thick wall steels such as offshore structures and pressure Presented at the Seventh International Conference on vessels [ 1 ] . Reasons of these rapid developments are based on their positive ...
... developed and applied to fabrication of thick wall steels such as offshore structures and pressure Presented at the Seventh International Conference on vessels [ 1 ] . Reasons of these rapid developments are based on their positive ...
Page 95
... developed for Arctic offshore structures . Fundamental studies showed that the application of accelerated cooling process to extra low - carbon and niobium containing steel plates brought about high strength and excellent toughness ...
... developed for Arctic offshore structures . Fundamental studies showed that the application of accelerated cooling process to extra low - carbon and niobium containing steel plates brought about high strength and excellent toughness ...
Page 99
... developed steel plates Steel Plate Thick- ness Tensile Test Charpy Impact Test ( mm ) Y S ( MPa ) T S ( MPa ) Loca- tion VE - 60 ( J ) FATT ( ° C ) YS420MPa 30 450 559 1/4 t 274 -114 30 512 591 1/4 t 286 -102 YS460MPa 1/4 t 289 -87 50 ...
... developed steel plates Steel Plate Thick- ness Tensile Test Charpy Impact Test ( mm ) Y S ( MPa ) T S ( MPa ) Loca- tion VE - 60 ( J ) FATT ( ° C ) YS420MPa 30 450 559 1/4 t 274 -114 30 512 591 1/4 t 286 -102 YS460MPa 1/4 t 289 -87 50 ...
Contents
ADVANCED COMPOSITES | 1 |
PAS2m High Performance Prepreg and Composites | 9 |
ADVANCES IN WELDING TECHNOLOGY | 31 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
abrasion analysis Arctic Engineering as-welded assessment austenite axial behaviour bending brittle fracture brittle zones CGHAZ Charpy chord coarse grained HAZ concrete Conference on Offshore corrosion fatigue crack depth crack length crack propagation CTOD tests CTOD values curve cycles defect effect fabrication ferrite fiber Figure fracture initiation fracture mechanics fracture toughness fusion line geometry grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen ICCGHAZ impact increase load low carbon low toughness martensite material maximum Mechanics and Arctic niobium Offshore Mechanics offshore structures Oseberg parameters plastic plate thickness pop-in post weld heat preheat PWHT region residual stresses S-N curves sampled simulated steel plates stiffeners stress concentration stress intensity factor structural steels submerged arc welding surface notched Table temperature tensile thermal TMCP tubular joints weld metal weld toe weldability welded joints welding procedures weldments wide plate tests yield strength