Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 7, Part 3American Society of Mechanical Engineers, 1988 - Arctic regions |
From inside the book
Results 1-3 of 84
Page 45
... developed and applied to fabrication of thick wall steels such as offshore structures and Presented at the Seventh International Conference on Offshore Mechanics and Arctic Engineering Houston , Texas - February 7-12 , 1988 pressure ...
... developed and applied to fabrication of thick wall steels such as offshore structures and Presented at the Seventh International Conference on Offshore Mechanics and Arctic Engineering Houston , Texas - February 7-12 , 1988 pressure ...
Page 95
... developed for Arctic offshore structures . Fundamental studies showed that the application of accelerated cooling process to extra low - carbon and niobium containing steel plates brought about high strength and excellent toughness ...
... developed for Arctic offshore structures . Fundamental studies showed that the application of accelerated cooling process to extra low - carbon and niobium containing steel plates brought about high strength and excellent toughness ...
Page 99
... developed steel plates Steel Plate Thick- ness Tensile Test ( mm ) Y S ( MPa ) VE - 60 ( J ) FATT ( ° C ) YS420MPa 30 450 559 1 / 4t 274 -114 30 512 591 1/4 t 286 -102 YS460MPa 1/4 t 289 -87 50 477 578 1/2 t 202 -85 * Test Specimen ...
... developed steel plates Steel Plate Thick- ness Tensile Test ( mm ) Y S ( MPa ) VE - 60 ( J ) FATT ( ° C ) YS420MPa 30 450 559 1 / 4t 274 -114 30 512 591 1/4 t 286 -102 YS460MPa 1/4 t 289 -87 50 477 578 1/2 t 202 -85 * Test Specimen ...
Contents
ADVANCED COMPOSITES | 1 |
A Study of the MultiLayered GRP Composite Cylindrical Vessel | 13 |
Resistance of Composite Structures to Impact Loads | 19 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
abrasion analysis as-welded assessment austenite axial base metal behaviour bending boron brittle fracture brittle zones CGHAZ Charpy chemical composition chord coarse grained HAZ concrete Conference on Offshore crack growth crack length CTOD tests CTOD values curve cycle defect effect fabrication ferrite fiber Figure fracture initiation fracture mechanics fracture toughness fusion line grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen ICCGHAZ impact increase layup load low carbon low toughness martensite material maximum Mechanics and Arctic method niobium Offshore Mechanics offshore structures Oseberg parameters plastic plate thickness pop-in post weld heat preheat PWHT region residual stresses sampled simulated solidification cracking steel plates stiffeners stress concentration stress intensity factor submerged arc welding surface notched Table temperature tensile thermal TMCP transverse tubular joints weld metal weld toe weldability welded joints welding procedures weldments wide plate tests yield strength