... effect in machine components and welded joints are reviewed , and some engineering rules dealing with this effect are discussed . Prediction models for fatigue life including crack initiation and crack propagation stages have been used ...
... effect in machine components and welded joints are reviewed , and some engineering rules dealing with this effect are discussed . Prediction models for fatigue life including crack initiation and crack propagation stages have been used ...
Page 368
... EFFECTS Three types of size effects influence the fatigue behavior : The statistical or volume size effect The technological or material size effect The stress gradient effect The Statistical Size Effect The statistical size effect ...
... EFFECTS Three types of size effects influence the fatigue behavior : The statistical or volume size effect The technological or material size effect The stress gradient effect The Statistical Size Effect The statistical size effect ...
Page 371
... effect , as shown in Fig . 8. The change in n from the value given by Eq.20 depends on the actual values of K and a1 . The curve in Fig.8 = was computed with Kt 2.2 and ai = 0.1 mm . Also shown in Fig.8 is the effect of scaling a with ...
... effect , as shown in Fig . 8. The change in n from the value given by Eq.20 depends on the actual values of K and a1 . The curve in Fig.8 = was computed with Kt 2.2 and ai = 0.1 mm . Also shown in Fig.8 is the effect of scaling a with ...
Contents
ADVANCED COMPOSITES | 1 |
A Study of the MultiLayered GRP Composite Cylindrical Vessel | 13 |
Resistance of Composite Structures to Impact Loads | 19 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
addition analysis applied areas assessment base bending brittle calculated carbon carried Charpy chemical chord coarse grained compared composite concrete considered cooling crack tip critical CTOD curve cycle defect depth determined developed direction distribution effect element energy Engineering examined fabrication factor failure fatigue crack ferrite Figure fracture mechanics fracture toughness fusion geometry growth hardness heat input higher impact increase initiation length load lower material maximum measured Mechanics method microstructures normal notch observed obtained occur offshore parameters performed plastic plate position present pressure problem procedure production properties range reduced region Research respectively sampled shown shows simulated specific specimens steel steel plates stiffeners strain strength stress structures surface Table temperature tensile thickness tubular values weld metal welded joints weldments wide yield zone