Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 7, Part 3American Society of Mechanical Engineers, 1988 - Arctic regions |
From inside the book
Results 1-3 of 84
Page 185
... toughness at the intercritical and at coarse grained simulation temperatures . It should be noted that the test ... fracture toughness . The coarse grained part of the HAZ and the intercritical part of the HAZ may show reduced fracture ...
... toughness at the intercritical and at coarse grained simulation temperatures . It should be noted that the test ... fracture toughness . The coarse grained part of the HAZ and the intercritical part of the HAZ may show reduced fracture ...
Page 495
... fracture The necessity of an appropriate toughness requirement for preventing service failure is well - understood . However , it is one of the most important questions how to carry out fracture toughness testing . In particular fracture ...
... fracture The necessity of an appropriate toughness requirement for preventing service failure is well - understood . However , it is one of the most important questions how to carry out fracture toughness testing . In particular fracture ...
Page 501
... toughness SCA Evaluating effect of LBZ on fracture performance Fatigue CTOD test Deep - notched bending CTOD tests K ... toughness and scatter behavior of LBZ toughness . To detect lower bound toughness of LBZ To detect short brittle ...
... toughness SCA Evaluating effect of LBZ on fracture performance Fatigue CTOD test Deep - notched bending CTOD tests K ... toughness and scatter behavior of LBZ toughness . To detect lower bound toughness of LBZ To detect short brittle ...
Contents
ADVANCED COMPOSITES | 1 |
PAS2m High Performance Prepreg and Composites | 9 |
ADVANCES IN WELDING TECHNOLOGY | 31 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
abrasion analysis Arctic Engineering as-welded assessment austenite axial behaviour bending brittle fracture brittle zones CGHAZ Charpy chord coarse grained HAZ concrete Conference on Offshore corrosion fatigue crack depth crack length crack propagation CTOD tests CTOD values curve cycles defect effect fabrication ferrite fiber Figure fracture initiation fracture mechanics fracture toughness fusion line geometry grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen ICCGHAZ impact increase load low carbon low toughness martensite material maximum Mechanics and Arctic niobium Offshore Mechanics offshore structures Oseberg parameters plastic plate thickness pop-in post weld heat preheat PWHT region residual stresses S-N curves sampled simulated steel plates stiffeners stress concentration stress intensity factor structural steels submerged arc welding surface notched Table temperature tensile thermal TMCP tubular joints weld metal weld toe weldability welded joints welding procedures weldments wide plate tests yield strength