Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 7, Part 3American Society of Mechanical Engineers, 1988 - Arctic regions |
From inside the book
Results 1-3 of 83
Page 92
... fusion boundary and intercritically reheated coarse grained heat affected zone ( ICCGHAZ ) at the middle thickness in the as - welded condition . The absorbed energy at -60 ° C exceeded 50 J at the three positions . Table 5 Chemical ...
... fusion boundary and intercritically reheated coarse grained heat affected zone ( ICCGHAZ ) at the middle thickness in the as - welded condition . The absorbed energy at -60 ° C exceeded 50 J at the three positions . Table 5 Chemical ...
Page 289
... fusion line and in the weld metal , 0.5 mm above the fusion line respectively . The idea was to simulate a crack in a LBZ , and a crack growing into a LBZ respectively . The typical resulting pre - fatigue crack positions , after some ...
... fusion line and in the weld metal , 0.5 mm above the fusion line respectively . The idea was to simulate a crack in a LBZ , and a crack growing into a LBZ respectively . The typical resulting pre - fatigue crack positions , after some ...
Page 350
... fusion line hardness of EH 34S welded joint has the high- est value of 230 Hv and the hardness of base metal has the lowest value of 150 Hv . The Microstructure Properties of Welded Joints Typical microstructures of SM 58Q and EH 34S ...
... fusion line hardness of EH 34S welded joint has the high- est value of 230 Hv and the hardness of base metal has the lowest value of 150 Hv . The Microstructure Properties of Welded Joints Typical microstructures of SM 58Q and EH 34S ...
Contents
ADVANCED COMPOSITES | 1 |
A Study of the MultiLayered GRP Composite Cylindrical Vessel | 13 |
Resistance of Composite Structures to Impact Loads | 19 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
abrasion analysis as-welded assessment austenite axial base metal behaviour bending boron brittle fracture brittle zones CGHAZ Charpy chemical composition chord coarse grained HAZ concrete Conference on Offshore crack growth crack length CTOD tests CTOD values curve cycle defect effect fabrication ferrite fiber Figure fracture initiation fracture mechanics fracture toughness fusion line grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen ICCGHAZ impact increase layup load low carbon low toughness martensite material maximum Mechanics and Arctic method niobium Offshore Mechanics offshore structures Oseberg parameters plastic plate thickness pop-in post weld heat preheat PWHT region residual stresses sampled simulated solidification cracking steel plates stiffeners stress concentration stress intensity factor submerged arc welding surface notched Table temperature tensile thermal TMCP transverse tubular joints weld metal weld toe weldability welded joints welding procedures weldments wide plate tests yield strength