Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 7, Part 3American Society of Mechanical Engineers, 1988 - Arctic regions |
From inside the book
Results 1-3 of 83
Page 92
... fusion boundary and intercritically reheated coarse grained heat affected zone ( ICCGHAZ ) at the middle thickness in the as - welded condition . The absorbed energy at -60 ° C exceeded 50 J at the three positions . Table 5 Chemical ...
... fusion boundary and intercritically reheated coarse grained heat affected zone ( ICCGHAZ ) at the middle thickness in the as - welded condition . The absorbed energy at -60 ° C exceeded 50 J at the three positions . Table 5 Chemical ...
Page 289
... fusion line and in the weld metal , 0.5 mm above the fusion line respectively . The idea was to simulate a crack in a LBZ , and a crack growing into a LBZ respectively . The typical resulting pre - fatigue crack positions , after some ...
... fusion line and in the weld metal , 0.5 mm above the fusion line respectively . The idea was to simulate a crack in a LBZ , and a crack growing into a LBZ respectively . The typical resulting pre - fatigue crack positions , after some ...
Page 350
... fusion line hardness of EH 34S welded joint has the high- est value of 230 Hv and the hardness of base metal has the lowest value of 150 Hv . The Microstructure Properties of Welded Joints Typical microstructures of SM 58Q and EH 34S ...
... fusion line hardness of EH 34S welded joint has the high- est value of 230 Hv and the hardness of base metal has the lowest value of 150 Hv . The Microstructure Properties of Welded Joints Typical microstructures of SM 58Q and EH 34S ...
Contents
ADVANCED COMPOSITES | 1 |
A Study of the MultiLayered GRP Composite Cylindrical Vessel | 13 |
Resistance of Composite Structures to Impact Loads | 19 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
addition analysis applied areas assessment base bending brittle calculated carbon carried Charpy chemical chord coarse grained compared composite concrete considered cooling crack tip critical CTOD curve cycle defect depth determined developed direction distribution effect element energy Engineering examined fabrication factor failure fatigue crack ferrite Figure fracture mechanics fracture toughness fusion geometry growth hardness heat input higher impact increase initiation length load lower material maximum measured Mechanics method microstructures normal notch observed obtained occur offshore parameters performed plastic plate position present pressure problem procedure production properties range reduced region Research respectively sampled shown shows simulated specific specimens steel steel plates stiffeners strain strength stress structures surface Table temperature tensile thickness tubular values weld metal welded joints weldments wide yield zone