Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 7, Part 3American Society of Mechanical Engineers, 1988 - Arctic regions |
From inside the book
Results 1-3 of 81
Page 129
... measured with both reflections . In order to derive strains from measured inter- planar spacings a reference spacing must be obtained . An average lattice parameter was computed from all the measured spacings in all three directions ...
... measured with both reflections . In order to derive strains from measured inter- planar spacings a reference spacing must be obtained . An average lattice parameter was computed from all the measured spacings in all three directions ...
Page 130
... measured . This process , conventionally used for X - ray stress analysis where the set of ( hkl ) planes is often not aligned with the ideal texture , yields effec- tive elastic constants for translating effects in one set of grains to ...
... measured . This process , conventionally used for X - ray stress analysis where the set of ( hkl ) planes is often not aligned with the ideal texture , yields effec- tive elastic constants for translating effects in one set of grains to ...
Page 261
... measured CTOD value were the location of the fatigue crack tip relative to the fusion line and the microstructure adjacent to and slightly ahead of the crack tip . Consideration of the detailed results demonstrates the sensitivity of ...
... measured CTOD value were the location of the fatigue crack tip relative to the fusion line and the microstructure adjacent to and slightly ahead of the crack tip . Consideration of the detailed results demonstrates the sensitivity of ...
Contents
ADVANCED COMPOSITES | 1 |
A Study of the MultiLayered GRP Composite Cylindrical Vessel | 13 |
Resistance of Composite Structures to Impact Loads | 19 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
abrasion analysis as-welded assessment austenite axial base metal behaviour bending boron brittle fracture brittle zones CGHAZ Charpy chemical composition chord coarse grained HAZ concrete Conference on Offshore crack growth crack length CTOD tests CTOD values curve cycle defect effect fabrication ferrite fiber Figure fracture initiation fracture mechanics fracture toughness fusion line grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen ICCGHAZ impact increase layup load low carbon low toughness martensite material maximum Mechanics and Arctic method niobium Offshore Mechanics offshore structures Oseberg parameters plastic plate thickness pop-in post weld heat preheat PWHT region residual stresses sampled simulated solidification cracking steel plates stiffeners stress concentration stress intensity factor submerged arc welding surface notched Table temperature tensile thermal TMCP transverse tubular joints weld metal weld toe weldability welded joints welding procedures weldments wide plate tests yield strength