Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 7, Part 3American Society of Mechanical Engineers, 1988 - Arctic regions |
From inside the book
Results 1-3 of 89
Page 122
... produced . Acceptance of the steel was conditional on the successful completion of the tests . Butt welds were produced by steelmakers or their sub - contractors with half K preparations on 25mm and K preparations ( see Fig . 2 ) on 40 ...
... produced . Acceptance of the steel was conditional on the successful completion of the tests . Butt welds were produced by steelmakers or their sub - contractors with half K preparations on 25mm and K preparations ( see Fig . 2 ) on 40 ...
Page 124
... produced by the ingot route . At C , all plates over 70mm thick and any plate weighing more than 13 tonnes were produced by ingot route . Ingot material was tested in both the steelmakers ' WT and in the SCT . No low toughness tests ...
... produced by the ingot route . At C , all plates over 70mm thick and any plate weighing more than 13 tonnes were produced by ingot route . Ingot material was tested in both the steelmakers ' WT and in the SCT . No low toughness tests ...
Page 209
... produced a ferritic - pearlitic microstructure of ASTM grain size 8-9 with a mean hardness of 172 HVO , 5 . The quenched and tempered steel B has a ferritic - bainitic microstructure with well defined areas of ferrite with aligned ...
... produced a ferritic - pearlitic microstructure of ASTM grain size 8-9 with a mean hardness of 172 HVO , 5 . The quenched and tempered steel B has a ferritic - bainitic microstructure with well defined areas of ferrite with aligned ...
Contents
ADVANCED COMPOSITES | 1 |
PAS2m High Performance Prepreg and Composites | 9 |
ADVANCES IN WELDING TECHNOLOGY | 31 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
abrasion analysis Arctic Engineering as-welded assessment austenite axial behaviour bending brittle fracture brittle zones CGHAZ Charpy chord coarse grained HAZ concrete Conference on Offshore corrosion fatigue crack depth crack length crack propagation CTOD tests CTOD values curve cycles defect effect fabrication ferrite fiber Figure fracture initiation fracture mechanics fracture toughness fusion line geometry grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen ICCGHAZ impact increase load low carbon low toughness martensite material maximum Mechanics and Arctic niobium Offshore Mechanics offshore structures Oseberg parameters plastic plate thickness pop-in post weld heat preheat PWHT region residual stresses S-N curves sampled simulated steel plates stiffeners stress concentration stress intensity factor structural steels submerged arc welding surface notched Table temperature tensile thermal TMCP tubular joints weld metal weld toe weldability welded joints welding procedures weldments wide plate tests yield strength