Page 122
... produced . Acceptance of the steel was conditional on the successful completion of the tests . Butt welds were produced by steelmakers or their sub - contractors with half K preparations on 25mm and K preparations ( see Fig . 2 ) on 40 ...
... produced . Acceptance of the steel was conditional on the successful completion of the tests . Butt welds were produced by steelmakers or their sub - contractors with half K preparations on 25mm and K preparations ( see Fig . 2 ) on 40 ...
Page 124
... produced by the ingot route . At C , all plates over 70mm thick and any plate weighing more than 13 tonnes were produced by ingot route . Ingot material was tested in both the steelmakers ' WT and in the SCT . No low toughness tests ...
... produced by the ingot route . At C , all plates over 70mm thick and any plate weighing more than 13 tonnes were produced by ingot route . Ingot material was tested in both the steelmakers ' WT and in the SCT . No low toughness tests ...
Page 209
... produced a ferritic - pearlitic microstructure of ASTM grain size 8-9 with a mean hardness of 172 HVO , 5 . The quenched and tempered steel B has a ferritic - bainitic microstructure with well defined areas of ferrite with aligned ...
... produced a ferritic - pearlitic microstructure of ASTM grain size 8-9 with a mean hardness of 172 HVO , 5 . The quenched and tempered steel B has a ferritic - bainitic microstructure with well defined areas of ferrite with aligned ...
Contents
ADVANCED COMPOSITES | 1 |
A Study of the MultiLayered GRP Composite Cylindrical Vessel | 13 |
Resistance of Composite Structures to Impact Loads | 19 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
addition analysis applied areas assessment base bending brittle calculated carbon carried Charpy chemical chord coarse grained compared composite concrete considered cooling crack tip critical CTOD curve cycle defect depth determined developed direction distribution effect element energy Engineering examined fabrication factor failure fatigue crack ferrite Figure fracture mechanics fracture toughness fusion geometry growth hardness heat input higher impact increase initiation length load lower material maximum measured Mechanics method microstructures normal notch observed obtained occur offshore parameters performed plastic plate position present pressure problem procedure production properties range reduced region Research respectively sampled shown shows simulated specific specimens steel steel plates stiffeners strain strength stress structures surface Table temperature tensile thickness tubular values weld metal welded joints weldments wide yield zone