THE INFLUENCE OF REDUCED CARBON EQUIVALENT ON HAZ CRACKING IN STRUCTURAL STEELS P. H. M. Hart and I. S. Matharu The Welding Institute , Abington Cambridge , England A. R. Jones , Formerly of TWI , now at UKAEA Northern Research Lab ...
THE INFLUENCE OF REDUCED CARBON EQUIVALENT ON HAZ CRACKING IN STRUCTURAL STEELS P. H. M. Hart and I. S. Matharu The Welding Institute , Abington Cambridge , England A. R. Jones , Formerly of TWI , now at UKAEA Northern Research Lab ...
Page 185
Local " brittle " zones Recommendations Examinations carried out have shown that low carbon controlled rolled and accelerated cooled steel i.e. the Oseberg Grade I steel under certain circumstances may exhibit local zones of reduced ...
Local " brittle " zones Recommendations Examinations carried out have shown that low carbon controlled rolled and accelerated cooled steel i.e. the Oseberg Grade I steel under certain circumstances may exhibit local zones of reduced ...
Page 210
The specimen diameter at mid-length was reduced to 6,4 mm over a length of 10 mm to aid in obtaining fracture in the center of the simulated portion . The minimum diameter of the reduced section was measured to the nearest 0,01 mm .
The specimen diameter at mid-length was reduced to 6,4 mm over a length of 10 mm to aid in obtaining fracture in the center of the simulated portion . The minimum diameter of the reduced section was measured to the nearest 0,01 mm .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
ADVANCED COMPOSITES | 1 |
A Study of the MultiLayered GRP Composite Cylindrical Vessel | 13 |
Resistance of Composite Structures to Impact Loads | 19 |
Copyright | |
32 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied areas assessment base bending brittle calculated carbon carried Charpy chemical coarse grained compared composite concrete considered cooling crack tip critical CTOD curve cycles defect depth determined developed direction distribution effect element energy Engineering examined fabrication factor failure fatigue crack ferrite Figure fracture mechanics fracture toughness fusion geometry growth hardness heat input higher impact increase initiation length load lower material maximum measured Mechanics method microstructures normal notch observed obtained occur offshore offshore structures parameters performed plastic plate position present pressure problem procedure production properties range reduced region Research respectively sampled shown shows significant simulated specification specimens steel steel plates stiffeners strain strength stress structures surface Table temperature tensile thickness tubular values weld metal welded joints weldments wide yield zone
Bibliographic information
| Title | Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 7, Part 3 |
| Contributor | American Society of Mechanical Engineers. Offshore Mechanics and Arctic Engineering Division |
| Publisher | American Society of Mechanical Engineers, 1988 |
| Original from | the University of Michigan |
| Digitized | 3 Dec 2007 |
| Export Citation | BiBTeX EndNote RefMan |