... reduced as the carbon equivalent decreased although the extent of improvement was less than expected when judged by behaviour based on experience from older steels . It is considered that the main reason for a smaller than expected ...
... reduced as the carbon equivalent decreased although the extent of improvement was less than expected when judged by behaviour based on experience from older steels . It is considered that the main reason for a smaller than expected ...
Page 185
... reduced fracture toughness . The reduced fracture toughness in the coarse grained part of the HAZ is always due to a high portion of coarse grain size and / or coarce grained inter- critically reheated microstructures . The presence of ...
... reduced fracture toughness . The reduced fracture toughness in the coarse grained part of the HAZ is always due to a high portion of coarse grain size and / or coarce grained inter- critically reheated microstructures . The presence of ...
Page 210
... reduced to 6,4 mm over a length of 10 mm to aid in obtaining fracture in the center of the simulat- ed portion . The minimum diameter of the reduced section was measured to the nearest 0,01 mm . Although the base metal tensile specimen ...
... reduced to 6,4 mm over a length of 10 mm to aid in obtaining fracture in the center of the simulat- ed portion . The minimum diameter of the reduced section was measured to the nearest 0,01 mm . Although the base metal tensile specimen ...
Contents
ADVANCED COMPOSITES | 1 |
A Study of the MultiLayered GRP Composite Cylindrical Vessel | 13 |
Resistance of Composite Structures to Impact Loads | 19 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
addition analysis applied areas assessment base bending brittle calculated carbon carried Charpy chemical chord coarse grained compared composite concrete considered cooling crack tip critical CTOD curve cycle defect depth determined developed direction distribution effect element energy Engineering examined fabrication factor failure fatigue crack ferrite Figure fracture mechanics fracture toughness fusion geometry growth hardness heat input higher impact increase initiation length load lower material maximum measured Mechanics method microstructures normal notch observed obtained occur offshore parameters performed plastic plate position present pressure problem procedure production properties range reduced region Research respectively sampled shown shows simulated specific specimens steel steel plates stiffeners strain strength stress structures surface Table temperature tensile thickness tubular values weld metal welded joints weldments wide yield zone