... reduced as the carbon equivalent decreased although the extent of improvement was less than expected when judged by behaviour based on experience from older steels . It is considered that the main reason for a smaller than expected ...
... reduced as the carbon equivalent decreased although the extent of improvement was less than expected when judged by behaviour based on experience from older steels . It is considered that the main reason for a smaller than expected ...
Page 185
... reduced fracture toughness . The reduced fracture toughness in the coarse grained part of the HAZ is always due to a high portion of coarse grain size and / or coarce grained inter- critically reheated microstructures . The presence of ...
... reduced fracture toughness . The reduced fracture toughness in the coarse grained part of the HAZ is always due to a high portion of coarse grain size and / or coarce grained inter- critically reheated microstructures . The presence of ...
Page 210
... reduced to 6,4 mm over a length of 10 mm to aid in obtaining fracture in the center of the simulat- ed portion . The minimum diameter of the reduced section was measured to the nearest 0,01 mm . Although the base metal tensile specimen ...
... reduced to 6,4 mm over a length of 10 mm to aid in obtaining fracture in the center of the simulat- ed portion . The minimum diameter of the reduced section was measured to the nearest 0,01 mm . Although the base metal tensile specimen ...
Contents
ADVANCED COMPOSITES | 1 |
PAS2m High Performance Prepreg and Composites | 9 |
ADVANCES IN WELDING TECHNOLOGY | 31 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
abrasion analysis Arctic Engineering as-welded assessment austenite axial behaviour bending brittle fracture brittle zones CGHAZ Charpy chord coarse grained HAZ concrete Conference on Offshore corrosion fatigue crack depth crack length crack propagation CTOD tests CTOD values curve cycles defect effect fabrication ferrite fiber Figure fracture initiation fracture mechanics fracture toughness fusion line geometry grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen ICCGHAZ impact increase load low carbon low toughness martensite material maximum Mechanics and Arctic niobium Offshore Mechanics offshore structures Oseberg parameters plastic plate thickness pop-in post weld heat preheat PWHT region residual stresses S-N curves sampled simulated steel plates stiffeners stress concentration stress intensity factor structural steels submerged arc welding surface notched Table temperature tensile thermal TMCP tubular joints weld metal weld toe weldability welded joints welding procedures weldments wide plate tests yield strength