... sampled is GCHAZ whereas the WI proposal mentioned only that the desired microstructure is sampled within the middle 60 % of the specimen and the test should attempt to maximise the microstructural region sampled . The EEMUA ...
... sampled is GCHAZ whereas the WI proposal mentioned only that the desired microstructure is sampled within the middle 60 % of the specimen and the test should attempt to maximise the microstructural region sampled . The EEMUA ...
Page 201
... sampled , % Fig.2 . CTOD versus per cent grain coarsened HAZ sampled by fatigue crack in the 50mm thick steel A. ( ) Assumed within the bulk of the specimen The peak temperature used in the second cycle for the ICGCHAZ simulation was ...
... sampled , % Fig.2 . CTOD versus per cent grain coarsened HAZ sampled by fatigue crack in the 50mm thick steel A. ( ) Assumed within the bulk of the specimen The peak temperature used in the second cycle for the ICGCHAZ simulation was ...
Page 261
... sampled . However , at higher temperatures it would seem that ' pop - ins ' are achieved when larger amounts of coarse grain are sampled and low toughness fracture can be prevented when only small amounts are present . An effect of ...
... sampled . However , at higher temperatures it would seem that ' pop - ins ' are achieved when larger amounts of coarse grain are sampled and low toughness fracture can be prevented when only small amounts are present . An effect of ...
Contents
ADVANCED COMPOSITES | 1 |
A Study of the MultiLayered GRP Composite Cylindrical Vessel | 13 |
Resistance of Composite Structures to Impact Loads | 19 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
abrasion analysis as-welded assessment austenite axial base metal behaviour bending boron brittle fracture brittle zones CGHAZ Charpy chemical composition chord coarse grained HAZ concrete Conference on Offshore crack growth crack length CTOD tests CTOD values curve cycle defect effect fabrication ferrite fiber Figure fracture initiation fracture mechanics fracture toughness fusion line grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen ICCGHAZ impact increase layup load low carbon low toughness martensite material maximum Mechanics and Arctic method niobium Offshore Mechanics offshore structures Oseberg parameters plastic plate thickness pop-in post weld heat preheat PWHT region residual stresses sampled simulated solidification cracking steel plates stiffeners stress concentration stress intensity factor submerged arc welding surface notched Table temperature tensile thermal TMCP transverse tubular joints weld metal weld toe weldability welded joints welding procedures weldments wide plate tests yield strength