Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 7, Part 3American Society of Mechanical Engineers, 1988 - Arctic regions |
From inside the book
Results 1-3 of 35
Page 195
... sampled is GCHAZ whereas the WI proposal mentioned only that the desired microstructure is sampled within the middle 60 % of the specimen and the test should attempt to maximise the microstructural region sampled . The EEMUA ...
... sampled is GCHAZ whereas the WI proposal mentioned only that the desired microstructure is sampled within the middle 60 % of the specimen and the test should attempt to maximise the microstructural region sampled . The EEMUA ...
Page 201
... sampled , % Fig.2 . CTOD versus per cent grain coarsened HAZ sampled by fatigue crack in the 50mm thick steel A. ( ) Assumed within the bulk of the specimen The peak temperature used in the second cycle for the ICGCHAZ simulation was ...
... sampled , % Fig.2 . CTOD versus per cent grain coarsened HAZ sampled by fatigue crack in the 50mm thick steel A. ( ) Assumed within the bulk of the specimen The peak temperature used in the second cycle for the ICGCHAZ simulation was ...
Page 261
... sampled . However , at higher temperatures it would seem that ' pop - ins ' are achieved when larger amounts of coarse grain are sampled and low toughness fracture can be prevented when only small amounts are present . An effect of ...
... sampled . However , at higher temperatures it would seem that ' pop - ins ' are achieved when larger amounts of coarse grain are sampled and low toughness fracture can be prevented when only small amounts are present . An effect of ...
Contents
ADVANCED COMPOSITES | 1 |
A Study of the MultiLayered GRP Composite Cylindrical Vessel | 13 |
Resistance of Composite Structures to Impact Loads | 19 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
addition analysis applied areas assessment base bending brittle calculated carbon carried Charpy chemical chord coarse grained compared composite concrete considered cooling crack tip critical CTOD curve cycle defect depth determined developed direction distribution effect element energy Engineering examined fabrication factor failure fatigue crack ferrite Figure fracture mechanics fracture toughness fusion geometry growth hardness heat input higher impact increase initiation length load lower material maximum measured Mechanics method microstructures normal notch observed obtained occur offshore parameters performed plastic plate position present pressure problem procedure production properties range reduced region Research respectively sampled shown shows simulated specific specimens steel steel plates stiffeners strain strength stress structures surface Table temperature tensile thickness tubular values weld metal welded joints weldments wide yield zone