... surface notched bead in groove weldments BxB CTOD specimens with an EDM notch ( a / W = 0.06 ) , b ) surface notched buttweldments BxB CTOD specimens with an EDM notch ( a / W = 0.06 ) and a fatigue notch ( a / W 0.3 ) , c ) through ...
... surface notched bead in groove weldments BxB CTOD specimens with an EDM notch ( a / W = 0.06 ) , b ) surface notched buttweldments BxB CTOD specimens with an EDM notch ( a / W = 0.06 ) and a fatigue notch ( a / W 0.3 ) , c ) through ...
Page 277
... area Notch toughness at -40 ° c1 ) ( MPa ) ( MPa ) ( % ) ( x ) ( J ) A 377 495 32 - 227 B 353 498 29 76 238 C 377 501 34 233 D 332 522 32 162 - - - it is a preferred position for weld defects surface irregularities give high stress ...
... area Notch toughness at -40 ° c1 ) ( MPa ) ( MPa ) ( % ) ( x ) ( J ) A 377 495 32 - 227 B 353 498 29 76 238 C 377 501 34 233 D 332 522 32 162 - - - it is a preferred position for weld defects surface irregularities give high stress ...
Page 279
... notch for the surface notched BxB CTOD specimens in the coarse grained zone of the buttweldments . SMAW ( left ) , SAW ( right ) . 4.4 CTOD for buttweldments surface notch a / W - 0.3 The next step was to substitute the shallow surface EDM ...
... notch for the surface notched BxB CTOD specimens in the coarse grained zone of the buttweldments . SMAW ( left ) , SAW ( right ) . 4.4 CTOD for buttweldments surface notch a / W - 0.3 The next step was to substitute the shallow surface EDM ...
Contents
ADVANCED COMPOSITES | 1 |
PAS2m High Performance Prepreg and Composites | 9 |
ADVANCES IN WELDING TECHNOLOGY | 31 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
abrasion analysis Arctic Engineering as-welded assessment austenite axial behaviour bending brittle fracture brittle zones CGHAZ Charpy chord coarse grained HAZ concrete Conference on Offshore corrosion fatigue crack depth crack length crack propagation CTOD tests CTOD values curve cycles defect effect fabrication ferrite fiber Figure fracture initiation fracture mechanics fracture toughness fusion line geometry grain coarsened HAZ HAZ toughness heat affected zone heat input hydrogen ICCGHAZ impact increase load low carbon low toughness martensite material maximum Mechanics and Arctic niobium Offshore Mechanics offshore structures Oseberg parameters plastic plate thickness pop-in post weld heat preheat PWHT region residual stresses S-N curves sampled simulated steel plates stiffeners stress concentration stress intensity factor structural steels submerged arc welding surface notched Table temperature tensile thermal TMCP tubular joints weld metal weld toe weldability welded joints welding procedures weldments wide plate tests yield strength