Notch In several cases it was observed that ductile crack growth could occur through the coarse grained zone without triggering a brittle fracture , fig 13 . The majority of brittle fractures were preferenti . ally initiated in the ...
Notch In several cases it was observed that ductile crack growth could occur through the coarse grained zone without triggering a brittle fracture , fig 13 . The majority of brittle fractures were preferenti . ally initiated in the ...
Page 522
5.0 OOO O 8 000 1.0 0.5 zone Critical COD , 0c ( mm ) As was shown earlier , cleavage fracture initiation can be assumed to take place when maximum tensile stress at the notch - tip ( om ) attains the critical fracture stress ( op ) .
5.0 OOO O 8 000 1.0 0.5 zone Critical COD , 0c ( mm ) As was shown earlier , cleavage fracture initiation can be assumed to take place when maximum tensile stress at the notch - tip ( om ) attains the critical fracture stress ( op ) .
Page 525
INFLUENCE OF LOCAL BRITTLE ZONES ON PLATE TOUGHNESS APPLICATION TO WELDED STRUCTURES L. Devillers , D. Kaplan , and E. Maas ... ACTUAL IDEALIZED CONFIGURATION CONFIGURATION brittle base weld metal HAZ zone meto1 Toughness is most often ...
INFLUENCE OF LOCAL BRITTLE ZONES ON PLATE TOUGHNESS APPLICATION TO WELDED STRUCTURES L. Devillers , D. Kaplan , and E. Maas ... ACTUAL IDEALIZED CONFIGURATION CONFIGURATION brittle base weld metal HAZ zone meto1 Toughness is most often ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
ADVANCED COMPOSITES | 1 |
A Study of the MultiLayered GRP Composite Cylindrical Vessel | 13 |
Resistance of Composite Structures to Impact Loads | 19 |
Copyright | |
32 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied areas assessment base bending brittle calculated carbon carried Charpy chemical coarse grained compared composite concrete considered cooling crack tip critical CTOD curve cycles defect depth determined developed direction distribution effect element energy Engineering examined fabrication factor failure fatigue crack ferrite Figure fracture mechanics fracture toughness fusion geometry growth hardness heat input higher impact increase initiation length load lower material maximum measured Mechanics method microstructures normal notch observed obtained occur offshore offshore structures parameters performed plastic plate position present pressure problem procedure production properties range reduced region Research respectively sampled shown shows significant simulated specification specimens steel steel plates stiffeners strain strength stress structures surface Table temperature tensile thickness tubular values weld metal welded joints weldments wide yield zone
Bibliographic information
| Title | Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 7, Part 3 |
| Contributor | American Society of Mechanical Engineers. Offshore Mechanics and Arctic Engineering Division |
| Publisher | American Society of Mechanical Engineers, 1988 |
| Original from | the University of Michigan |
| Digitized | 3 Dec 2007 |
| Export Citation | BiBTeX EndNote RefMan |