... elongation averages 40 per cent . Cold - working increases the hardness of aluminum to 40 Bhn and decreases the elongation to 5 per cent . One of the limitations of aluminum is that , at elevated temperatures , the mechanical properties ...
... elongation averages 40 per cent . Cold - working increases the hardness of aluminum to 40 Bhn and decreases the elongation to 5 per cent . One of the limitations of aluminum is that , at elevated temperatures , the mechanical properties ...
Page 150
... Elongation % 50 Reduction of area % 70 9281 40 50 54 12 18 50 55 28 21 50 Hardness Rockwell F40 F60 F71 F80 Impact - Izod ft - lb 40 40 Hard - drawn condition * Tensile strength Yield strength Elongation Reduction of area Hardness ...
... Elongation % 50 Reduction of area % 70 9281 40 50 54 12 18 50 55 28 21 50 Hardness Rockwell F40 F60 F71 F80 Impact - Izod ft - lb 40 40 Hard - drawn condition * Tensile strength Yield strength Elongation Reduction of area Hardness ...
Page 250
... Elongation Hardness Service temperatures a . Intermittent b . Continuous c . Minimum Specific gravity psi % 700-1250 230-400 Shore A 50-80 ° F 명 명명 300 ° F 212 ° F -65 1.35 be used at temperatures from -65 up to 300 ° F and is of ...
... Elongation Hardness Service temperatures a . Intermittent b . Continuous c . Minimum Specific gravity psi % 700-1250 230-400 Shore A 50-80 ° F 명 명명 300 ° F 212 ° F -65 1.35 be used at temperatures from -65 up to 300 ° F and is of ...
Contents
FANSTEEL METALLURGICAL CORPORA | 1 |
HERCULES POWDER COMPANY | 8 |
JESSOP STEEL COMPANY | 16 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
abrasion acid addition alkalies alloys aluminum aluminum alloys amounts annealed anode applications atmospheres attack austenitic base brasses carbon carbon steel cast iron cause cements cent characteristics chemical resistance chloride coat cold-working combination common composition compounds concentrations conductivity construction containing continuous cooling copper corrosion resistance cracking ductility effect electrical elevated Elongation environments equipment excellent expansion fabrication given grades gray greater handled hardness heat heat-treatment improved increase industries lead less limited lower machining material maximum mechanical properties metal method Monel nickel nitric normally occurs operating organic oxidizing paint performed physical pipe pitting plastic prevent produced protection range readily recommended reducing removed rubber salts severe silicon solutions solvents stainless steels strength psi stress structure suitable sulfuric acid superior surface Table temperature tensile strength thermal tion titanium Type Typical welding widely wrought zinc