Materials Selection for Process Plants |
From inside the book
Results 1-3 of 38
Page 127
... Hastelloy C " is comparable to that of " Hastelloy B " and about 50 per cent greater than that of Type 316 stainless steel . Wrought " Has- telloy C " is quite hard and has decreased impact values . In the cast form , the strength of ...
... Hastelloy C " is comparable to that of " Hastelloy B " and about 50 per cent greater than that of Type 316 stainless steel . Wrought " Has- telloy C " is quite hard and has decreased impact values . In the cast form , the strength of ...
Page 128
... Hastelloy W " or 25-20 stainless- steel electrodes perform satisfactorily . The cold - worked or welded part should not be placed in service in the " as - is " condition . Heat - treatment is necessary to restore ductility , ma ...
... Hastelloy W " or 25-20 stainless- steel electrodes perform satisfactorily . The cold - worked or welded part should not be placed in service in the " as - is " condition . Heat - treatment is necessary to restore ductility , ma ...
Page 306
... Hastelloy C annealing , 128 carbide precipitation , 127 composition , 126 corrosion resistance , 128 forming , 127 heat - treatment , 128 high temperature , 130 machining , 127 properties , 126 uses , 130 welding , 127 Hastelloy D ...
... Hastelloy C annealing , 128 carbide precipitation , 127 composition , 126 corrosion resistance , 128 forming , 127 heat - treatment , 128 high temperature , 130 machining , 127 properties , 126 uses , 130 welding , 127 Hastelloy D ...
Contents
FANSTEEL METALLURGICAL CORPORA | 1 |
HERCULES POWDER COMPANY | 8 |
JESSOP STEEL COMPANY | 16 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
abrasion acid addition alkalies alloys aluminum aluminum alloys amounts annealed anode applications atmospheres attack austenitic base brasses carbon carbon steel cast iron cause cements cent characteristics chemical resistance chloride coat cold-working combination common composition compounds concentrations conductivity construction containing continuous cooling copper corrosion resistance cracking ductility effect electrical elevated Elongation environments equipment excellent expansion fabrication given grades gray greater handled hardness heat heat-treatment improved increase industries lead less limited lower machining material maximum mechanical properties metal method Monel nickel nitric normally occurs operating organic oxidizing paint performed physical pipe pitting plastic prevent produced protection range readily recommended reducing removed rubber salts severe silicon solutions solvents stainless steels strength psi stress structure suitable sulfuric acid superior surface Table temperature tensile strength thermal tion titanium Type Typical welding widely wrought zinc