Materials Selection for Process Plants |
From inside the book
Results 1-3 of 84
Page 85
... Tensile strength psi X 103 70 75 115 75 Yield strength psi X 103 35 40 90 40 Elongation % 25 35 20 30 25 Reduction of area % 75 70 60 60 55 5835 95 125 110 50 95 65 20 15 55 25 Hardness Brinell 145 155 230 155 180 260 230 Impact - Izod ...
... Tensile strength psi X 103 70 75 115 75 Yield strength psi X 103 35 40 90 40 Elongation % 25 35 20 30 25 Reduction of area % 75 70 60 60 55 5835 95 125 110 50 95 65 20 15 55 25 Hardness Brinell 145 155 230 155 180 260 230 Impact - Izod ...
Page 141
... tensile values ranging from 13,000-33,000 psi in the annealed condi- tion . Where fully hardened by heat - treatment , the tensile strengths range from 42,000-83,000 psi . In fact , hardened alloy 7075 has a tensile strength which is ...
... tensile values ranging from 13,000-33,000 psi in the annealed condi- tion . Where fully hardened by heat - treatment , the tensile strengths range from 42,000-83,000 psi . In fact , hardened alloy 7075 has a tensile strength which is ...
Page 146
... yield strengths of this latter alloy . Zinc is TABLE 12.9 . AVERAGE PHYSICAL AND MECHANICAL PROPERTIES OF SOME SAND ... strength psi X 103 19 21 Yield strength psi X 103 Elongation % 8 243 14 Reduction of % 2321 20 area Hardness Brinell ...
... yield strengths of this latter alloy . Zinc is TABLE 12.9 . AVERAGE PHYSICAL AND MECHANICAL PROPERTIES OF SOME SAND ... strength psi X 103 19 21 Yield strength psi X 103 Elongation % 8 243 14 Reduction of % 2321 20 area Hardness Brinell ...
Contents
FANSTEEL METALLURGICAL CORPORA | 1 |
HERCULES POWDER COMPANY | 8 |
JESSOP STEEL COMPANY | 16 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
abrasion acid addition alkalies alloys aluminum aluminum alloys amounts annealed anode applications atmospheres attack austenitic base brasses carbon carbon steel cast iron cause cements cent characteristics chemical resistance chloride coat cold-working combination common composition compounds concentrations conductivity construction containing continuous cooling copper corrosion resistance cracking ductility effect electrical elevated Elongation environments equipment excellent expansion fabrication given grades gray greater handled hardness heat heat-treatment improved increase industries lead less limited lower machining material maximum mechanical properties metal method Monel nickel nitric normally occurs operating organic oxidizing paint performed physical pipe pitting plastic prevent produced protection range readily recommended reducing removed rubber salts severe silicon solutions solvents stainless steels strength psi stress structure suitable sulfuric acid superior surface Table temperature tensile strength thermal tion titanium Type Typical welding widely wrought zinc