Materials Selection for Process Plants |
From inside the book
Results 1-3 of 59
Page 90
... austenitic alloys are normally nonmagnetic , but cold - working tends to induce some TABLE 9.5 . NOMINAL COMPOSITION OF AUSTENITIC STAINLESS STEELS Carbon 90 MATERIALS SELECTION FOR PROCESS PLANTS Austenitic-300 Series.
... austenitic alloys are normally nonmagnetic , but cold - working tends to induce some TABLE 9.5 . NOMINAL COMPOSITION OF AUSTENITIC STAINLESS STEELS Carbon 90 MATERIALS SELECTION FOR PROCESS PLANTS Austenitic-300 Series.
Page 94
... austenitic stainless steels exhibit greatest corrosion resistance when the carbon is completely dissolved in the matrix . When Types 304 , 316 and 317 are heated by welding or hot - forming within the temperature range of 800-1600 ° F ...
... austenitic stainless steels exhibit greatest corrosion resistance when the carbon is completely dissolved in the matrix . When Types 304 , 316 and 317 are heated by welding or hot - forming within the temperature range of 800-1600 ° F ...
Page 96
... austenitic stainless steel surface is exceedingly dirty or scaly , 2 per cent hydrofluoric acid may be added to the nitric acid solu- tion . This latter solution is very strong and it will tend to etch the metal surface . Thus , the ...
... austenitic stainless steel surface is exceedingly dirty or scaly , 2 per cent hydrofluoric acid may be added to the nitric acid solu- tion . This latter solution is very strong and it will tend to etch the metal surface . Thus , the ...
Contents
FANSTEEL METALLURGICAL CORPORA | 1 |
HERCULES POWDER COMPANY | 8 |
JESSOP STEEL COMPANY | 16 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
abrasion acid addition alkalies alloys aluminum aluminum alloys amounts annealed anode applications atmospheres attack austenitic base brasses carbon carbon steel cast iron cause cements cent characteristics chemical resistance chloride coat cold-working combination common composition compounds concentrations conductivity construction containing continuous cooling copper corrosion resistance cracking ductility effect electrical elevated Elongation environments equipment excellent expansion fabrication given grades gray greater handled hardness heat heat-treatment improved increase industries lead less limited lower machining material maximum mechanical properties metal method Monel nickel nitric normally occurs operating organic oxidizing paint performed physical pipe pitting plastic prevent produced protection range readily recommended reducing removed rubber salts severe silicon solutions solvents stainless steels strength psi stress structure suitable sulfuric acid superior surface Table temperature tensile strength thermal tion titanium Type Typical welding widely wrought zinc