Materials Selection for Process Plants |
From inside the book
Results 1-3 of 39
Page 154
... brass 70 30 Yellow brass 65 35 Muntz metal 60 40 Naval brass 60 39.25 Tin Manganese bronze 58.5 39 Tin 0.75 1.00 Manganese 0.50 max Iron 1.40 alpha - beta brasses . Brasses are available in the 154 MATERIALS SELECTION FOR PROCESS PLANTS ...
... brass 70 30 Yellow brass 65 35 Muntz metal 60 40 Naval brass 60 39.25 Tin Manganese bronze 58.5 39 Tin 0.75 1.00 Manganese 0.50 max Iron 1.40 alpha - beta brasses . Brasses are available in the 154 MATERIALS SELECTION FOR PROCESS PLANTS ...
Page 156
... brasses with a zinc content below 20 per cent have a chemical resistance paralleling that of electrolytic tough - pitch copper , these brasses are relatively unaffected by dezincification and are used at elevated tem- peratures in the ...
... brasses with a zinc content below 20 per cent have a chemical resistance paralleling that of electrolytic tough - pitch copper , these brasses are relatively unaffected by dezincification and are used at elevated tem- peratures in the ...
Page 157
... brasses and can be cold - worked to a greater degree . Spring - tempered alloys are available with a tensile value approaching 120,000 psi . The ductility is lower than that of the brasses . These alloys retain their properties at low ...
... brasses and can be cold - worked to a greater degree . Spring - tempered alloys are available with a tensile value approaching 120,000 psi . The ductility is lower than that of the brasses . These alloys retain their properties at low ...
Contents
FANSTEEL METALLURGICAL CORPORA | 1 |
HERCULES POWDER COMPANY | 8 |
JESSOP STEEL COMPANY | 16 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
abrasion acid addition alkalies alloys aluminum aluminum alloys amounts annealed anode applications atmospheres attack austenitic base brasses carbon carbon steel cast iron cause cements cent characteristics chemical resistance chloride coat cold-working combination common composition compounds concentrations conductivity construction containing continuous cooling copper corrosion resistance cracking ductility effect electrical elevated Elongation environments equipment excellent expansion fabrication given grades gray greater handled hardness heat heat-treatment improved increase industries lead less limited lower machining material maximum mechanical properties metal method Monel nickel nitric normally occurs operating organic oxidizing paint performed physical pipe pitting plastic prevent produced protection range readily recommended reducing removed rubber salts severe silicon solutions solvents stainless steels strength psi stress structure suitable sulfuric acid superior surface Table temperature tensile strength thermal tion titanium Type Typical welding widely wrought zinc