Materials Selection for Process Plants |
From inside the book
Results 1-3 of 42
Page 89
... cooling rapidly . The hardness is lowered , the internal stresses are relieved and the impact properties are improved . Welded structures are very ductile when held at 400-500 ° F . However , after holding in the range 750-1100 ° F for ...
... cooling rapidly . The hardness is lowered , the internal stresses are relieved and the impact properties are improved . Welded structures are very ductile when held at 400-500 ° F . However , after holding in the range 750-1100 ° F for ...
Page 150
... cooled , it becomes brittle because of a coarsely crystalline structure that develops during slow cooling . If quickly cooled , however , copper is soft , malleable and ductile . Upon cold - working , the elongation decreases from 55-15 ...
... cooled , it becomes brittle because of a coarsely crystalline structure that develops during slow cooling . If quickly cooled , however , copper is soft , malleable and ductile . Upon cold - working , the elongation decreases from 55-15 ...
Page 213
... cooling , they harden and take the shape of the mold or form . While hot or warm , the thermoplastics are soft , pliable , and cannot be handled ; they must be cooled in place . The thermoplastics can be reheated , remelted and reformed ...
... cooling , they harden and take the shape of the mold or form . While hot or warm , the thermoplastics are soft , pliable , and cannot be handled ; they must be cooled in place . The thermoplastics can be reheated , remelted and reformed ...
Contents
FANSTEEL METALLURGICAL CORPORA | 1 |
HERCULES POWDER COMPANY | 8 |
JESSOP STEEL COMPANY | 16 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
abrasion acid addition alkalies alloys aluminum aluminum alloys amounts annealed anode applications atmospheres attack austenitic base brasses carbon carbon steel cast iron cause cements cent characteristics chemical resistance chloride coat cold-working combination common composition compounds concentrations conductivity construction containing continuous cooling copper corrosion resistance cracking ductility effect electrical elevated Elongation environments equipment excellent expansion fabrication given grades gray greater handled hardness heat heat-treatment improved increase industries lead less limited lower machining material maximum mechanical properties metal method Monel nickel nitric normally occurs operating organic oxidizing paint performed physical pipe pitting plastic prevent produced protection range readily recommended reducing removed rubber salts severe silicon solutions solvents stainless steels strength psi stress structure suitable sulfuric acid superior surface Table temperature tensile strength thermal tion titanium Type Typical welding widely wrought zinc