... filler metals with melting points in excess of 800 ° F , while soldering covers the use of filler materials below 800 ° F . Com- monly , in brazing and soldering , the joints are made by flowing the filler metal between closely mated ...
... filler metals with melting points in excess of 800 ° F , while soldering covers the use of filler materials below 800 ° F . Com- monly , in brazing and soldering , the joints are made by flowing the filler metal between closely mated ...
Page 152
... filler metal ; however , phosphorus - de- oxidized copper filler metal is sometimes employed for maximum corrosion resistance . Heat - treatment is not customarily performed on copper . The metal does not normally require annealing or ...
... filler metal ; however , phosphorus - de- oxidized copper filler metal is sometimes employed for maximum corrosion resistance . Heat - treatment is not customarily performed on copper . The metal does not normally require annealing or ...
Page 214
... filler , and catalyst . They are care- fully mixed , molded into shape , and cured under heat and pressure or by heat alone . Items used in quantity are often produced by the common com- pression- and transfer - molding techniques ...
... filler , and catalyst . They are care- fully mixed , molded into shape , and cured under heat and pressure or by heat alone . Items used in quantity are often produced by the common com- pression- and transfer - molding techniques ...
Contents
FANSTEEL METALLURGICAL CORPORA | 1 |
HERCULES POWDER COMPANY | 8 |
JESSOP STEEL COMPANY | 16 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
abrasion acid addition alkalies alloys aluminum aluminum alloys amounts annealed anode applications atmospheres attack austenitic base brasses carbon carbon steel cast iron cause cements cent characteristics chemical resistance chloride coat cold-working combination common composition compounds concentrations conductivity construction containing continuous cooling copper corrosion resistance cracking ductility effect electrical elevated Elongation environments equipment excellent expansion fabrication given grades gray greater handled hardness heat heat-treatment improved increase industries lead less limited lower machining material maximum mechanical properties metal method Monel nickel nitric normally occurs operating organic oxidizing paint performed physical pipe pitting plastic prevent produced protection range readily recommended reducing removed rubber salts severe silicon solutions solvents stainless steels strength psi stress structure suitable sulfuric acid superior surface Table temperature tensile strength thermal tion titanium Type Typical welding widely wrought zinc