Materials Selection for Process Plants |
From inside the book
Results 1-3 of 17
Page 209
... Furane mortars are prepared at the place of use . Two parts by weight of powder and one part by weight of liquid resin are mixed to a smooth consistency . The mortar must be troweled and used immediately . To avoid premature setting of ...
... Furane mortars are prepared at the place of use . Two parts by weight of powder and one part by weight of liquid resin are mixed to a smooth consistency . The mortar must be troweled and used immediately . To avoid premature setting of ...
Page 301
... furane , 209 phenolic , 208 polyester , 209 silicate , 206 sulfur , 207 Chemical resistance , paints alkyd , 271 ... furane , 218 phenolic , 215 polycarbonate , 238 polyester , 219 polyethylene , 227 polypropylene , 237 polyvinyl ...
... furane , 209 phenolic , 208 polyester , 209 silicate , 206 sulfur , 207 Chemical resistance , paints alkyd , 271 ... furane , 218 phenolic , 215 polycarbonate , 238 polyester , 219 polyethylene , 227 polypropylene , 237 polyvinyl ...
Page 305
... furane , 208 phenolic , 208 polyester , 209 silicate , 206 sulfur , 207 Formulation , paints alkyd , 270 asphalt ... Furane cements chemical resistance , 209 formulation , 208 temperature limitations , 209 Furane plastics abrasion ...
... furane , 208 phenolic , 208 polyester , 209 silicate , 206 sulfur , 207 Formulation , paints alkyd , 270 asphalt ... Furane cements chemical resistance , 209 formulation , 208 temperature limitations , 209 Furane plastics abrasion ...
Contents
FANSTEEL METALLURGICAL CORPORA | 1 |
HERCULES POWDER COMPANY | 8 |
JESSOP STEEL COMPANY | 16 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
abrasion acid addition alkalies alloys aluminum aluminum alloys amounts annealed anode applications atmospheres attack austenitic base brasses carbon carbon steel cast iron cause cements cent characteristics chemical resistance chloride coat cold-working combination common composition compounds concentrations conductivity construction containing continuous cooling copper corrosion resistance cracking ductility effect electrical elevated Elongation environments equipment excellent expansion fabrication given grades gray greater handled hardness heat heat-treatment improved increase industries lead less limited lower machining material maximum mechanical properties metal method Monel nickel nitric normally occurs operating organic oxidizing paint performed physical pipe pitting plastic prevent produced protection range readily recommended reducing removed rubber salts severe silicon solutions solvents stainless steels strength psi stress structure suitable sulfuric acid superior surface Table temperature tensile strength thermal tion titanium Type Typical welding widely wrought zinc