Materials Selection for Process Plants |
From inside the book
Results 1-3 of 70
Page 124
... gases . “ Hastelloy B " resists the attack of flue gases , ammonia , carbon monoxide , carbon dioxide , and hydrocar- bons . It has outstanding resistance to wet hydrogen - chloride gas , but very poor resistance to chlorine . In the ...
... gases . “ Hastelloy B " resists the attack of flue gases , ammonia , carbon monoxide , carbon dioxide , and hydrocar- bons . It has outstanding resistance to wet hydrogen - chloride gas , but very poor resistance to chlorine . In the ...
Page 168
... gas - shielded - arc - welding is especially suitable for use on thin gauge metal and where flux cannot be used ... gases can be more corrosive ; often , a dark but harmless film is formed on the exposed surfaces . Marine and rural ...
... gas - shielded - arc - welding is especially suitable for use on thin gauge metal and where flux cannot be used ... gases can be more corrosive ; often , a dark but harmless film is formed on the exposed surfaces . Marine and rural ...
Page 170
... gases and about 1900 ° F in sulfur - free oxidizing atmospheres . Sulfur gases cause attack at temperatures of 600-700 ° F ; reducing conditions cause more damage than oxidizing conditions . Up to 800 ° F , nickel is free from corrosive ...
... gases and about 1900 ° F in sulfur - free oxidizing atmospheres . Sulfur gases cause attack at temperatures of 600-700 ° F ; reducing conditions cause more damage than oxidizing conditions . Up to 800 ° F , nickel is free from corrosive ...
Contents
FANSTEEL METALLURGICAL CORPORA | 1 |
HERCULES POWDER COMPANY | 8 |
JESSOP STEEL COMPANY | 16 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
abrasion acid addition alkalies alloys aluminum aluminum alloys amounts annealed anode applications atmospheres attack austenitic base brasses carbon carbon steel cast iron cause cements cent characteristics chemical resistance chloride coat cold-working combination common composition compounds concentrations conductivity construction containing continuous cooling copper corrosion resistance cracking ductility effect electrical elevated Elongation environments equipment excellent expansion fabrication given grades gray greater handled hardness heat heat-treatment improved increase industries lead less limited lower machining material maximum mechanical properties metal method Monel nickel nitric normally occurs operating organic oxidizing paint performed physical pipe pitting plastic prevent produced protection range readily recommended reducing removed rubber salts severe silicon solutions solvents stainless steels strength psi stress structure suitable sulfuric acid superior surface Table temperature tensile strength thermal tion titanium Type Typical welding widely wrought zinc