Page 85
... Hardened and tem- pered condition Tensile strength psi X 103 180 180 195 180 235 200 285 Yield strength psi X 103 ... hardened and tempered condition . In the annealed state , the tensile strengths range from 70,000-115,000 psi ; when ...
... Hardened and tem- pered condition Tensile strength psi X 103 180 180 195 180 235 200 285 Yield strength psi X 103 ... hardened and tempered condition . In the annealed state , the tensile strengths range from 70,000-115,000 psi ; when ...
Page 141
... hardened by heat - treatment , the tensile strengths range from 42,000-83,000 psi . In fact , hardened alloy 7075 has a tensile strength which is comparable to that of hardened carbon steel and above that of structural steel . The ...
... hardened by heat - treatment , the tensile strengths range from 42,000-83,000 psi . In fact , hardened alloy 7075 has a tensile strength which is comparable to that of hardened carbon steel and above that of structural steel . The ...
Page 147
... hardened wrought aluminum alloys ; notable exceptions are those of the hardened high - strength wrought alloys . All aluminum alloy castings can be machined on standard shop equip- ment . High speed steel cutting tools can be used for ...
... hardened wrought aluminum alloys ; notable exceptions are those of the hardened high - strength wrought alloys . All aluminum alloy castings can be machined on standard shop equip- ment . High speed steel cutting tools can be used for ...
Contents
FANSTEEL METALLURGICAL CORPORA | 1 |
HERCULES POWDER COMPANY | 8 |
JESSOP STEEL COMPANY | 16 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
abrasion acid addition alkalies alloys aluminum aluminum alloys amounts annealed anode applications atmospheres attack austenitic base brasses carbon carbon steel cast iron cause cements cent characteristics chemical resistance chloride coat cold-working combination common composition compounds concentrations conductivity construction containing continuous cooling copper corrosion resistance cracking ductility effect electrical elevated Elongation environments equipment excellent expansion fabrication given grades gray greater handled hardness heat heat-treatment improved increase industries lead less limited lower machining material maximum mechanical properties metal method Monel nickel nitric normally occurs operating organic oxidizing paint performed physical pipe pitting plastic prevent produced protection range readily recommended reducing removed rubber salts severe silicon solutions solvents stainless steels strength psi stress structure suitable sulfuric acid superior surface Table temperature tensile strength thermal tion titanium Type Typical welding widely wrought zinc