Annealing will lower the casting hardness and increase the machinability ; where
annealing is indicated , the operation should be performed after rough machining
and before final finishing . Although at one time welding of gray - iron castings ...
Annealing will lower the casting hardness and increase the machinability ; where
annealing is indicated , the operation should be performed after rough machining
and before final finishing . Although at one time welding of gray - iron castings ...
Page 122
Upon removal from the heat , the hot - forming operations must be performed
immediately , for the allowable working ... however , because of the wrought alloy
' s greater strength , more power is required to perform the shaping operations .
Upon removal from the heat , the hot - forming operations must be performed
immediately , for the allowable working ... however , because of the wrought alloy
' s greater strength , more power is required to perform the shaping operations .
Page 127
During heating , it is important to use low sulfur fuels and to keep the flame from
impinging on the work . Hot - forming must be performed immediately after the
metal is removed from the furnace . The wrought alloy exhibits good ductility and
is ...
During heating , it is important to use low sulfur fuels and to keep the flame from
impinging on the work . Hot - forming must be performed immediately after the
metal is removed from the furnace . The wrought alloy exhibits good ductility and
is ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
abrasion acid addition alkalies alloys aluminum annealed anode applications atmospheres attack austenitic base brasses carbon carbon steel cast iron cause cements cent characteristics chemical resistance chloride cleaning coat combination common COMPANY compounds concentrations conductivity construction containing continuous cooling copper corrosion corrosion resistance cost cracking ductility effect electrical elevated Elongation environments equipment excellent exposure fabrication film given grades gray greater handled hardness heat heat-treatment improved increase industries lead limited lining lower machining material maximum mechanical properties metal method Monel natural nickel nitric normally occurs operating organic oxidizing paint performed physical pipe plastic prevent protection range readily recommended reducing removed rubber salts severe silicon sodium hypochlorite solutions solvents stainless steels stress structure suitable sulfuric acid superior surface Table temperature tensile strength thermal tion titanium Type Typical welding widely wrought zinc
Bibliographic information
| Title | Materials Selection for Process Plants |
| Author | Russell E. Gackenbach |
| Publisher | Reinhold Publishing Corporation, 1960 |
| Original from | the University of Wisconsin - Madison |
| Digitized | 23 Apr 2008 |
| ISBN | 0442152604, 9780442152604 |
| Length | 318 pages |
| Export Citation | BiBTeX EndNote RefMan |