Materials Selection for Process Plants |
From inside the book
Results 1-3 of 52
Page 66
... superior to the unalloyed flake irons and equivalent to that of the heat - resisting flake irons . Spheroidal cast irons have been placed in service at temperatures up to 1100 ° F ; in fact , a ductile iron containing 6 per cent silicon ...
... superior to the unalloyed flake irons and equivalent to that of the heat - resisting flake irons . Spheroidal cast irons have been placed in service at temperatures up to 1100 ° F ; in fact , a ductile iron containing 6 per cent silicon ...
Page 160
... superior to that of the phosphor bronzes . It is believed that a thin adherent oxide film is responsible for this minor improvement . This alloy shows in- creased corrosion in alkaline media and , in certain solutions , dealuminiza ...
... superior to that of the phosphor bronzes . It is believed that a thin adherent oxide film is responsible for this minor improvement . This alloy shows in- creased corrosion in alkaline media and , in certain solutions , dealuminiza ...
Page 273
... superior resistance to heat , oxidation and oils . Standard neoprene cannot be used as a coating because it has limited solu- bility in organic solvents . A sulfur - modified version is quite soluble and readily compounded into a paint ...
... superior resistance to heat , oxidation and oils . Standard neoprene cannot be used as a coating because it has limited solu- bility in organic solvents . A sulfur - modified version is quite soluble and readily compounded into a paint ...
Contents
FANSTEEL METALLURGICAL CORPORA | 1 |
HERCULES POWDER COMPANY | 8 |
JESSOP STEEL COMPANY | 16 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing Brinell bronzes carbide carbon steel cast iron cathodic cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking Density ductility effect electrodes elevated temperatures Elongation environments epoxies equipment fabrication ferritic filler film furane given in Table grades graphite gray iron handled hardened hardness Hastelloy heat heat-treatment Inconel increase inhibitors lead machining Manganese material mechanical properties metal surface Modulus of elasticity Monel Ni-Resist nickel nitric acid oxidizing paint phenolics phosphoric physical and mechanical pipe plastic process industries produced rate of attack readily reducing Reduction of area resin rubber salts sea water silicon sodium solutions solvents stainless steels stress structure sulfuric acid tensile strength Tensile strength psi thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium