Glass, Volume 17Minoru Tomozawa, Robert Heward Doremus |
From inside the book
Results 1-3 of 61
Page 187
... Table VII . The high - thermal expansion of most of these glasses is probably due to the large amount of alkali inclusions . These glasses are recommended for coating or soldering to high - expansion metals such as copper and aluminum ...
... Table VII . The high - thermal expansion of most of these glasses is probably due to the large amount of alkali inclusions . These glasses are recommended for coating or soldering to high - expansion metals such as copper and aluminum ...
Page 233
... Table XXXIII did not show any significant TABLE XXXII LEAD BORATE - BASED GLASSES AS BASE Glasses For VITREOUS SOLDER Glass GLASS COMPOSITES " Composition ( wt % ) PbO B203 SiO2 Al2O3 ZnO Thermal expansion Dilatometric coefficient ...
... Table XXXIII did not show any significant TABLE XXXII LEAD BORATE - BASED GLASSES AS BASE Glasses For VITREOUS SOLDER Glass GLASS COMPOSITES " Composition ( wt % ) PbO B203 SiO2 Al2O3 ZnO Thermal expansion Dilatometric coefficient ...
Page 243
... Table XLII and used for sealing at a tempera- ture higher than the melting point of material A. A small amount of refractory oxides could also be added , as shown in Table XLII , to adjust the thermal expansion characteristics . It was ...
... Table XLII and used for sealing at a tempera- ture higher than the melting point of material A. A small amount of refractory oxides could also be added , as shown in Table XLII , to adjust the thermal expansion characteristics . It was ...
Contents
Solubility Models | 9 |
Effect of Experimental Variables on Gas Mobility in Vitreous Materials | 16 |
Phase Separation and Crystallization | 26 |
Copyright | |
18 other sections not shown
Common terms and phrases
activation energy addition alkali alkali ions alkali silicate glasses annealing atom band bleaching BOHC borate boron borosilicate glass cation Ceram Chem chemical durability components concentration crystallization curve decrease defect centers devitrifiable solder glasses Doremus effect ESR spectra eV band experimental Friebele fused silica glass surface glass systems glasses containing grinding Griscom heat treatment helium hole center hole trapped hydrogen hyperfine immiscibility immiscibility boundary increase indentation irradiation lapping hardness layer measured mole Na₂O Non-Cryst nonbridging oxygen nucleation observed optical absorption oxide glasses oxygen particle PbTiO3 permeability phase separation Phys polishing grains polishing rate powder properties radiation radiation-induced reaction samples Section Shelby shown in Fig silicate glasses SiO2 sodium softening point solder glass composites solubility spectrum spinodal decomposition structure studies Table Takamori thermal expansion coefficient tion Tomozawa U.S. Patent viscosity vitreous silica vitreous solder glass volume loss