Reaction of Water with Glass : Some Experimental Methods and Results At least
three different steps are involved in the reaction of water with a silicate glass
containing alkali ions : The first is ion exchange of hydronium ( H3O + ) or
hydrogen ...
Reaction of Water with Glass : Some Experimental Methods and Results At least
three different steps are involved in the reaction of water with a silicate glass
containing alkali ions : The first is ion exchange of hydronium ( H3O + ) or
hydrogen ...
Page 197
However , in the Cu - containing analogs , changes in O2 - treatment
temperatures cause significant changes in the softening point of each of the
glasses , the changes being most dramatic for those glasses having higher Cu
contents . As the ...
However , in the Cu - containing analogs , changes in O2 - treatment
temperatures cause significant changes in the softening point of each of the
glasses , the changes being most dramatic for those glasses having higher Cu
contents . As the ...
Page 205
TABLE XVII COMPARISON OF TI , O - CONTAINING GLASSES Which Show
HIGHLY DIFFERENT SOLUBILITY IN WATER Glass Softening point . ( °C ) no .
Composition ( wl % ) Coefficient of - thermal expansion " PbO B20 , SiO2 Al2O3
TeO2 ...
TABLE XVII COMPARISON OF TI , O - CONTAINING GLASSES Which Show
HIGHLY DIFFERENT SOLUBILITY IN WATER Glass Softening point . ( °C ) no .
Composition ( wl % ) Coefficient of - thermal expansion " PbO B20 , SiO2 Al2O3
TeO2 ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Solubility Models | 9 |
Effect of Experimental Variables on Gas Mobility in Vitreous Materials | 16 |
Phase Separation and Crystallization | 26 |
Copyright | |
14 other sections not shown
Other editions - View all
Common terms and phrases
absorption activation addition alkali amount appears atom band borate calculated Ceram chemical coefficient components composition concentration constant containing crystallization curve decrease defect defect centers dependence described determined devitrifiable solder glasses diffusion discussed durability effect electron energy et al example experimental Figure function given glass composites grains grinding Griscom growth hardness heat helium hole immiscibility increase indentation intensity ions irradiation lapping lead loss lower material measured mechanism observed obtained optical oxide oxygen particle Patent phase phase separation Phys polishing rate properties radiation range reaction relationship removal reported samples sealing Shelby shown in Fig shows silica silicate glasses similar SiO2 sodium softening point solder glass solubility solution spectra spectrum structure studies suggested surface Table temperature thermal expansion tion trapped treatment various viscosity vitreous volume yield