Page 44
Depth ( um ) Fig . 4 . Profile of hydrogen and sodium ions in a soda - lime glass
held 560 hr in water at 90°C . ( From Lanford , 1978 . ) Points measured ; line
calculated from Eq . ( 21 ) with b = 10 % . Fractional sodium ion concentration + -
+ ...
Depth ( um ) Fig . 4 . Profile of hydrogen and sodium ions in a soda - lime glass
held 560 hr in water at 90°C . ( From Lanford , 1978 . ) Points measured ; line
calculated from Eq . ( 21 ) with b = 10 % . Fractional sodium ion concentration + -
+ ...
Page 157
The indentation depth was 3 . 3 um and the hump was 85 um wide and rose 0 . 3
um above the glass surface . Similar humps were observed in SK and BK glasses
. This phenomenon shows that Knoop indentation is related to plastic flow .
The indentation depth was 3 . 3 um and the hump was 85 um wide and rose 0 . 3
um above the glass surface . Similar humps were observed in SK and BK glasses
. This phenomenon shows that Knoop indentation is related to plastic flow .
Page 208
4 4 . 00 19 . 2 9 . 23 61 . 5 3 . 84 a Kataoka and Kawamoto ( 1955 ) . STRENGTH
( psi x103 ) STANDARD DEVIATION DEPTH REMOVED FROM 208 TAKESHI
TAKAMORI.
4 4 . 00 19 . 2 9 . 23 61 . 5 3 . 84 a Kataoka and Kawamoto ( 1955 ) . STRENGTH
( psi x103 ) STANDARD DEVIATION DEPTH REMOVED FROM 208 TAKESHI
TAKAMORI.
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Solubility Models | 9 |
Effect of Experimental Variables on Gas Mobility in Vitreous Materials | 16 |
Phase Separation and Crystallization | 26 |
Copyright | |
14 other sections not shown
Other editions - View all
Common terms and phrases
absorption activation addition alkali amount appears atom band borate calculated Ceram chemical coefficient components composition concentration constant containing crystallization curve decrease defect defect centers dependence described determined devitrifiable solder glasses diffusion discussed durability effect electron energy et al example experimental Figure function given glass composites grains grinding Griscom growth hardness heat helium hole immiscibility increase indentation intensity ions irradiation lapping lead loss lower material measured mechanism observed obtained optical oxide oxygen particle Patent phase phase separation Phys polishing rate properties radiation range reaction relationship removal reported samples sealing Shelby shown in Fig shows silica silicate glasses similar SiO2 sodium softening point solder glass solubility solution spectra spectrum structure studies suggested surface Table temperature thermal expansion tion trapped treatment various viscosity vitreous volume yield
Bibliographic information
| Title | Glass, Volume 17 Glass, Minoru Tomozawa Volume 12 of Treatise on materials science and technology |
| Editors | Minoru Tomozawa, Robert Heward Doremus |
| Publisher | Academic Press, 1979 |
| Original from | the University of Michigan |
| Digitized | 29 Nov 2007 |
| ISBN | 0123418127, 9780123418128 |
| Length | 362 pages |
| Export Citation | BiBTeX EndNote RefMan |