Glass, Volume 17Minoru Tomozawa, Robert Heward Doremus |
From inside the book
Results 1-3 of 45
Page 176
... expansion coefficient measured . They tested several sets of additivity factors previously proposed by plotting f , versus p1 , and found a striking linearity when the set of the factors by Dauvalter ( 1948 ) was used for the f ...
... expansion coefficient measured . They tested several sets of additivity factors previously proposed by plotting f , versus p1 , and found a striking linearity when the set of the factors by Dauvalter ( 1948 ) was used for the f ...
Page 190
... expansion solder glass in certain applications ( Landermann and Takamori , 1977 ) . One drawback of this preheat treatment for phase separation is that the glass becomes chemically less durable after phase separation ( Tomozawa and ...
... expansion solder glass in certain applications ( Landermann and Takamori , 1977 ) . One drawback of this preheat treatment for phase separation is that the glass becomes chemically less durable after phase separation ( Tomozawa and ...
Page 231
... expansion solder glasses based on the PbO- B2O3 - T120 system ( see Section II.A.2 ) were mixed with low - expansion oxides such as cordierite , fused silica , and lithium aluminosilicate ceramics to obtain solder glass composites ...
... expansion solder glasses based on the PbO- B2O3 - T120 system ( see Section II.A.2 ) were mixed with low - expansion oxides such as cordierite , fused silica , and lithium aluminosilicate ceramics to obtain solder glass composites ...
Contents
Solubility Models | 9 |
Effect of Experimental Variables on Gas Mobility in Vitreous Materials | 16 |
Phase Separation and Crystallization | 26 |
Copyright | |
18 other sections not shown
Common terms and phrases
activation energy addition alkali alkali ions alkali silicate glasses annealing atom band bleaching BOHC borate boron borosilicate glass cation Ceram Chem chemical durability components concentration crystallization curve decrease defect centers devitrifiable solder glasses Doremus effect ESR spectra eV band experimental Friebele fused silica glass surface glass systems glasses containing grinding Griscom heat treatment helium hole center hole trapped hydrogen hyperfine immiscibility immiscibility boundary increase indentation irradiation lapping hardness layer measured mole Na₂O Non-Cryst nonbridging oxygen nucleation observed optical absorption oxide glasses oxygen particle PbTiO3 permeability phase separation Phys polishing grains polishing rate powder properties radiation radiation-induced reaction samples Section Shelby shown in Fig silicate glasses SiO2 sodium softening point solder glass composites solubility spectrum spinodal decomposition structure studies Table Takamori thermal expansion coefficient tion Tomozawa U.S. Patent viscosity vitreous silica vitreous solder glass volume loss