Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 14, Part 3American Society of Mechanical Engineers, 1995 - Arctic regions |
From inside the book
Results 1-3 of 56
Page 149
... Corrosion , Mid- County Press , 1985 . J. J. Yang and W. H. Hartt , " Near - Threshold Fatigue Crack Growth of High Strength Steels in Sea Water , " Proc . of the 12th Int . Conf . on Offshore Mechanics and Arctic Engineering , Vol ...
... Corrosion , Mid- County Press , 1985 . J. J. Yang and W. H. Hartt , " Near - Threshold Fatigue Crack Growth of High Strength Steels in Sea Water , " Proc . of the 12th Int . Conf . on Offshore Mechanics and Arctic Engineering , Vol ...
Page 151
... corrosion fatigue of high strength structural steels in seawater is promoted by the uptake of hydrogen that results from applying cathodic protection ( CP ) to control corrosion . The research described in this paper has shown that not ...
... corrosion fatigue of high strength structural steels in seawater is promoted by the uptake of hydrogen that results from applying cathodic protection ( CP ) to control corrosion . The research described in this paper has shown that not ...
Page 152
... corrosion rate . Clearly , from the above considerations the presence of active populations of SRB in the local marine environment would be expected to have a strong influence on the corrosion fatigue performance of steel offshore ...
... corrosion rate . Clearly , from the above considerations the presence of active populations of SRB in the local marine environment would be expected to have a strong influence on the corrosion fatigue performance of steel offshore ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 14 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment austenitic axial behaviour bending brace calculated cathodic protection Charpy chord Corrosion Fatigue crack depth crack front crack growth rate crack propagation crack tip CTOD cycles defect deformation developed effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar notch offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions Proc procedure region repair residual stress ring-stiffened joints riser S-N curve sea water seawater shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile test results titanium TMCP tubular joints tested values weld metal weld toe welded joints weldment yield strength