Page 174
... connections have been presented by Lu ( 1995 ) . In the present paper , the results of the parameter studies on I - beam to RHS column connections loaded with axial compression on I - beams are discussed . Comparisons between these two ...
... connections have been presented by Lu ( 1995 ) . In the present paper , the results of the parameter studies on I - beam to RHS column connections loaded with axial compression on I - beams are discussed . Comparisons between these two ...
Page 175
... connections with ẞ < 0.93 , the failures of the connections are caused by the chord face yielding , while for connections with B = 0.93 , chord side wall failures occur . A typical load ( N ) - displacement ( A ) diagram obtained from ...
... connections with ẞ < 0.93 , the failures of the connections are caused by the chord face yielding , while for connections with B = 0.93 , chord side wall failures occur . A typical load ( N ) - displacement ( A ) diagram obtained from ...
Page 178
... connections with J > 0 . For negative load ratios however , the connection strength decreases significantly , linear with J. This multiplanar loading influence is described by equation ( 11 ) : f ( J ) = 1 + 0.37J J < 0 ( 11 ) TABLE 5 ...
... connections with J > 0 . For negative load ratios however , the connection strength decreases significantly , linear with J. This multiplanar loading influence is described by equation ( 11 ) : f ( J ) = 1 + 0.37J J < 0 ( 11 ) TABLE 5 ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 14 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment austenitic axial behaviour bending brace calculated cathodic protection Charpy chord Corrosion Fatigue crack depth crack front crack growth rate crack propagation crack tip CTOD cycles defect deformation developed effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar notch offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions Proc procedure region repair residual stress ring-stiffened joints riser S-N curve sea water seawater shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile test results titanium TMCP tubular joints tested values weld metal weld toe welded joints weldment yield strength