Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 14, Part 3American Society of Mechanical Engineers, 1995 - Arctic regions |
From inside the book
Results 1-3 of 93
Page 212
... cycles ) , no shift from the T ' curve is imposed since the in - air fatigue life is matched : see Fig . 11. At long lives , the S - N design curve is completed by extending the line in the very long fatigue life regime ( greater than ...
... cycles ) , no shift from the T ' curve is imposed since the in - air fatigue life is matched : see Fig . 11. At long lives , the S - N design curve is completed by extending the line in the very long fatigue life regime ( greater than ...
Page 375
... cycles hardness yield tensile ° C yield strength in MPa 500 impact trans . 450 HV10 strength strength temperature MPa MPa 50 J 100 J 400 DO 15 mm plate 50 mm plate -0-75 mm plate 750 1 166 427 534 -88 -75 350 750 3 163 393 533 -92 -75 ...
... cycles hardness yield tensile ° C yield strength in MPa 500 impact trans . 450 HV10 strength strength temperature MPa MPa 50 J 100 J 400 DO 15 mm plate 50 mm plate -0-75 mm plate 750 1 166 427 534 -88 -75 350 750 3 163 393 533 -92 -75 ...
Page 581
... CYCLES N K = 3.75 ( Pū.so ) K = 3.50 ( Pú.90 ) 53.7 5 པ་ 102 3 tion of number of cycles of fatigue life at a given stress range . Fig . 10 shows a typical fatigue life curve ( S - N - curve ) as ob- tained from the experiments . The ...
... CYCLES N K = 3.75 ( Pū.so ) K = 3.50 ( Pú.90 ) 53.7 5 པ་ 102 3 tion of number of cycles of fatigue life at a given stress range . Fig . 10 shows a typical fatigue life curve ( S - N - curve ) as ob- tained from the experiments . The ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
VOLUME IA OFFSHORE TECHNOLOGY VOLUME IIIMATERIALS ENGINEERING | 18 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
20 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment axial behaviour bending brace calculated cathodic protection Charpy chord crack depth crack growth rate crack initiation crack propagation crack tip CTOD cycles defect deformation developed ductility effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar normalised notch obtained offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions procedure ratio region repair residual stress ring-stiffened joints S-N curve sea water seawater shielding gas shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile TMCP tubular joints tested undermatched values weld metal weld toe welded joints weldment yield strength