... developed to facilitate evaluations of alternative repair methods for ship CSD . An interactive Personal Computer ( PC ) program identified as RMS ( Repair Management System ) has been developed to facilitate application of the SFA in ...
... developed to facilitate evaluations of alternative repair methods for ship CSD . An interactive Personal Computer ( PC ) program identified as RMS ( Repair Management System ) has been developed to facilitate application of the SFA in ...
Page 357
... developed by controlling the microstructure of the surface layers . The surface layer consists of ultra fine grain ferrite microstructure , which provides excellent fracture toughness even at cryogenic temperature . When an unstable ...
... developed by controlling the microstructure of the surface layers . The surface layer consists of ultra fine grain ferrite microstructure , which provides excellent fracture toughness even at cryogenic temperature . When an unstable ...
Page 363
... developed steel plate can be used for actual uses , as similar to conventional steel plates . CONCLUSIONS A new - type steel plate has been developed by controlling the microstructure of the surface layers . The plate has surface layers ...
... developed steel plate can be used for actual uses , as similar to conventional steel plates . CONCLUSIONS A new - type steel plate has been developed by controlling the microstructure of the surface layers . The plate has surface layers ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 14 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment austenitic axial behaviour bending brace calculated cathodic protection Charpy chord Corrosion Fatigue crack depth crack front crack growth rate crack propagation crack tip CTOD cycles defect deformation developed effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar notch offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions Proc procedure region repair residual stress ring-stiffened joints riser S-N curve sea water seawater shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile test results titanium TMCP tubular joints tested values weld metal weld toe welded joints weldment yield strength