Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 14, Part 3American Society of Mechanical Engineers, 1995 - Arctic regions |
From inside the book
Results 1-3 of 89
Page 12
... given on the use of grouted or mechanical clamps for repair , supplementing that given in Section 60 of the HSE Guidance . This is based on research undertaken in the mid 1980s [ 14 ] . High Strength Steels High strength steels are ...
... given on the use of grouted or mechanical clamps for repair , supplementing that given in Section 60 of the HSE Guidance . This is based on research undertaken in the mid 1980s [ 14 ] . High Strength Steels High strength steels are ...
Page 56
... given in Fig . 1 . The geometrical discontinuity causes the misfitting of deformation that is considerably influenced by the size fac- tors such as plate thickness , notch / crack size , net section size , etc. Moreover , the ...
... given in Fig . 1 . The geometrical discontinuity causes the misfitting of deformation that is considerably influenced by the size fac- tors such as plate thickness , notch / crack size , net section size , etc. Moreover , the ...
Page 504
... given chemical composition and thermal experience , it is possible to identify a specific weld metal oxygen range that will result in a high volume fraction of the desired acicular ferrite . This investigation was designed to develop an ...
... given chemical composition and thermal experience , it is possible to identify a specific weld metal oxygen range that will result in a high volume fraction of the desired acicular ferrite . This investigation was designed to develop an ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 14 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment austenitic axial behaviour bending brace calculated cathodic protection Charpy chord Corrosion Fatigue crack depth crack front crack growth rate crack propagation crack tip CTOD cycles defect deformation developed effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar notch offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions Proc procedure region repair residual stress ring-stiffened joints riser S-N curve sea water seawater shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile test results titanium TMCP tubular joints tested values weld metal weld toe welded joints weldment yield strength