... higher yield ratios ( YR ) . This has caused some concem and debate on their work hardening capacity and moreover , current material specification and design codes severely penalise their use by placing limits on YR and on allowable ...
... higher yield ratios ( YR ) . This has caused some concem and debate on their work hardening capacity and moreover , current material specification and design codes severely penalise their use by placing limits on YR and on allowable ...
Page 367
... higher strengths this specification requirement value is generally exceeded . Plate thickness also influences the level of yield strength and YR and this is illustrated in Figure 4 where data related to a particular strength grade shows ...
... higher strengths this specification requirement value is generally exceeded . Plate thickness also influences the level of yield strength and YR and this is illustrated in Figure 4 where data related to a particular strength grade shows ...
Page 435
... higher strength ( overmatching ) than the steel . In this case , the higher strength of WM compared to BM may provide an optimum weld joint performance by shielding short cracks or other planar faults from applied strains . But it is ...
... higher strength ( overmatching ) than the steel . In this case , the higher strength of WM compared to BM may provide an optimum weld joint performance by shielding short cracks or other planar faults from applied strains . But it is ...
Contents
FATIGUE GUIDANCE FOR OFFSHORE STRUCTURES | 1 |
OFFSHORE MECHANICS AND ARCTIC ENGINEERING | 14 |
STRUCTURAL INTEGRITY METHODS FOR WELDED COMPONENTS | 55 |
Copyright | |
15 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied assessment austenitic axial behaviour bending brace calculated cathodic protection Charpy chord Corrosion Fatigue crack depth crack front crack growth rate crack propagation crack tip CTOD cycles defect deformation developed effect Efthymiou equations evaluation experimental failure fatigue crack growth fatigue guidance fatigue lives fatigue strength fatigue tests Figure finite element finite element analysis fracture mechanics fracture toughness GCHAZ geometry hammer peening high strength steels hydrogen increase Laser welds load material measured method microstructure mismatch mixed mode multiplanar notch offshore structures parameters parametric equations parent plate peening pipe plate thickness predictions Proc procedure region repair residual stress ring-stiffened joints riser S-N curve sea water seawater shown in Fig strain stress concentration stress concentration factor stress intensity factor stress range surface cracks Table tensile test results titanium TMCP tubular joints tested values weld metal weld toe welded joints weldment yield strength